Research on reduction of Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> by biomass sawdust

The research on biomass reduction of Fe₂O₃ was carried out by using sawdust as reductant. The direct reducing agents in the biomass magnetization process were determined by comparing various biomass pyrolysis products with the reduction degree (divalent iron content in total iron), reduction temperature range and valence change of Fe₂O₃ in the reduction process. The microstructure variation of Fe₂O₃ at different stages was also analyzed by scanning electron microscopy (SEM). Nonisothermal thermogravimetric analysis (TGA) was applied to explore the thermal reduction process. The results show that the direct reducing substances in the biomass reaction with Fe₂O₃ are H₂ and bio-oil, and the reduction process can be divided into two steps: biomass pyrolyzing to release H₂ and bio-oil, and reductive volatiles reacting with Fe₂O₃. The two steps are relatively independent. The kinetic of the reduction reaction follows a first-order reaction kinetic model, with 88.99 kJ/mol activation energy and 9.55 × 10⁸ min^?1 frequency factor.     

Quantitative phase analysis of the calcium silicate slag as the residue of extracting alumina from high-alumina fly ash

Calcium silicate slag is the residue of process of pre-desilication alkali lime sintering applied in the high-alumina fly ash to extract the alumina. The quantitative phase analysis (QPA) of the calcium silicate slag has been performed by the Rietveld method based on the powder X-ray diffraction (XRD) with the aid of noncommercial software GSAS-EXPGUI. A known weight of crystalline internal standard (10% CaF₂) was added to the calcium silicate slag to calculate the fraction of amorphous phase and other crystalline phases on an absolute basis. Besides, the calcium silicate slag was characterized by X-ray fluorescence (XRF) and thermo gravimetric (TG) differential scanning calorimetry (DSC) to test the QPA results and investigate its other characters. Finally, the results show that the amorphous fraction is 17.5% (hereinafter, the percentages refer to the mass fraction), and the major crystalline phases detected in the calcium silicate slag consist of 23.5% Beta-Ca2SiO₄, 10.0% bredigite, 10.3% Ca₃Al₂O₆ (C₃A) and 21.6% CaCO₃.