<正>A high-strength Mg-15.3Gd-l.8Ag-0.3Zr(GQ152K,mass fraction) alloy was prepared by conventional ingot metallurgy process.The solution and aging(denoted as T6) treated alloy exhibits remarkable mechanical properties with ultimate tensile strength of 421 MPa and tensile yield strength of 309MPa.It has higher igniting temperature of 1208 K.Moreover,it can stand against flame at 1203 K for over 6 min in vertical burning tests, and its flammabiUty behavior is very similar to that of 6101A1 alloy.Vertical burning tests appear to be able to directly study the flammability behavior of Mg alloys and it appears to be a good approach to study the flammability behavior of Mg alloys in an aircraft fire accident. 相似文献
2.
The effects of RE on the microstrcture of as-cast Mg-8Zn-4Al magnesium alloys were investigated. The results show that the solidification range of Mg-8Zn-4Al-xRE alloys increases with RE additions. A binary eutectic reaction can arise and produce a new phase （Mg：Al：Zn：RE） and the temperature of phase transformation point of the new phase is 412.85 C. In Mg-8Zn-4Al-1.5RE alloy, a small amount of Mg：Al：Zn：RE phase and ε phases are found besides a（Mg）,φand r phases. Also microstructures of Mg-8Zn-4Al alloys can be refined by addition of 1.5% RE obviously. 相似文献
3.
IntroductionLost foam casting( LFC) process is a newtechnology that is different from the conventionalempty mould cavity casting completely.This tech-nology is an important orientation of casting tech-nology,and is called as casting technology for to-morrow.At present,the studies on LFC are fo-cused on casting techniques mainly[1～ 5] .There islittle information on the structure and mechanicalproperties of B31 9in LFC process.Now for alu-minum alloy in LFC process,the main problemsare se… 相似文献
4.
IntroductionMagnesium alloys are called green-engineeringmaterial with great development potential becauseof its low density, high specific strength and stiff-ness, superior damping capacity, good electromag-netic shielding characteristics and good machinabil-ity[1]. However, the number of commercially avail-able magnesium alloys is still limited especially forapplication at elevated temperatures. The applica-tions of most common magnesium alloys such asAZ91 and AM60 with outstanding mechani… 相似文献
5.
1