适于钢管高强混凝土的缓凝保塑高效减水剂的研制

将聚羧酸减水剂、葡萄糖酸钠、硫酸锌等按一定比例复合,研制出一种高减水率、低引气量的钢管混凝土专用缓凝保塑高效减水剂WUT-G(Ⅰ):配制C 50钢管混凝土时,其最佳掺量为0.9%~1.3%;配制C 60钢管混凝土时,其最佳掺量为1.2%~1.6%。所配制的混凝土具有良好的工作性能:初始坍落度大于23 cm、扩展度大于60 cm,5 h坍落度仍达14 cm以上,不离析、不泌水,满足钢管混凝土泵送施工工艺要求。同时,混凝土含气量小于1.8%,能有效减少钢管混凝土中普遍存在的混凝土与钢管壁脱粘现象的产生。

Development of High-Effective Retarder and Water-Reducer for Preparing High-Strength Concrete-Filled Steel Pipe

A new type of high-effective retarder and water-reducer with low air entraining content and high water reducing rate for preparing high-strength concretefilled steel pipe is developed by using of polycarboxylate water-reducer and sodium gluconate as well as zinc sulphate.Experimental results of this admixture show that,when a certain amount of the admixture ranged from 0.9% to 1.3% by the weight of cement is added for preparing C50 concrete-filled steel pipe while 1.2% to 1.6% for C60 concrete-filled steel pipe,fresh concrete has a perfect workability such as its initial slump is higher than 23 cm as well as initial flow is higher than 60 cm and its slump for 5 hours is above(14 cm,) which meets the needs of requirements of concrete pumping technique.Furthermore,the fresh concrete has a low air-content(lower 1.8%),which could have a chance to decrease the probability of separation of the concrete and steel pipe generally existed in concrete-filled steel pipe structure.