| S355J2W耐候钢焊接接头显微组织与力学性能 | |
| 引用本文： | 张励忠,刘博维,张淘,宋志坤,刘畅. S355J2W耐候钢焊接接头显微组织与力学性能[J]. 北方交通大学学报, 2012, 0(4): 127-130,134 |
| 作者姓名： | 张励忠 刘博维 张淘 宋志坤 刘畅 |
| 作者单位： | [1]北京交通大学机械与电子控制工程学院,北京100044 [2]北京科技大学腐蚀与防护中心,北京100083 |
| 基金项目： | 中国北车长春轨道客车股份有限公司合作项目 |
| 摘 要： | 通过拉伸、疲劳和金相检验试验,对S355J2W耐候钢、空冷状态焊接接头和退火状态焊接接头进行了显微组织和力学性能的研究.结果表明：两种状态焊接接头的力学性能都达到了要求,S355J2W耐候钢退火状态焊接接头的强度低于空冷状态焊接接头的强度;退火状态焊接接头的塑性好于空冷状态焊接接头的塑性;退火状态焊接接头的疲劳寿命低于空冷状态焊接接头的疲劳寿命;退火状态焊接接头与空冷状态焊接接头相比,每个区域的晶粒都有明显的细化和均匀化,空冷状态的焊接接头显微组织的晶界比较清晰. |
| 关 键 词： | S355J2W钢 焊接接头 力学性能 显微组织 |
Microstructures and mechanical properties of the welded joints of S355J2W steel |
|
| ZHANG Lizhong,LIU Bowei,ZHANG Tao,SONG Zhikun,LIU Chang. Microstructures and mechanical properties of the welded joints of S355J2W steel[J]. Journal of Northern Jiaotong University, 2012, 0(4): 127-130,134 | |
| Authors: | ZHANG Lizhong LIU Bowei ZHANG Tao SONG Zhikun LIU Chang |
| Affiliation: | 1. School of Mechanical ,Electronic and Control Engineering, Beijing Jiaotong University, Beijing 100044, China; 2. Center for Corrosion and Protection, University of Science and Technology Beijing, Beijing 100083, China) |
| Abstract: | In present work, the welded joints processed from 8355J2W steel were treated separately by air cooling and annealing. The investigation of the microstructure and mechanical properties of the welded joints were conducted through the tensile test, fatigue test and metallographic examination. The resuhs showed that the mechanic properties of the welded joints after both heat treatments had achieved the requiring standard. Compared to the welded ioint treated by air cooling, the annealed welded joint exhibited better plasticity, accompany with poorer strength. Through the fatigue test, it was revealed the air cooled welded ioint had comparatively longer fatigue life-time than the annealed one. The microstructure observation showed that the grain of all areas in annealed welded joint appeared more significant reduction in size and clearer homogenization, compared to the air cooled joint. Meanwhile, the grain boundary in air cooled welded joint was easier to observe than the annealed joint. |
| Keywords: | S355J2W steel welded joint mechanical property microstructure |