Experimental study on the impact characteristics of a sandwich composite with an aluminum foam core

The need for composites has been increasing in various industries because composites have good mechanical properties for their weight and superior stiffness and strength. The composites addressed in this study were multi-pore aluminum foam with a specific gravity of 1/10 composed of solid aluminum metal. This composite has excellent impact energy-absorption capability. In this study, impact tests on an aluminum foam core sandwich composite with a porous core were conducted to examine its mechanical properties. The specimen was a sandwich structure with an aluminum foam core, and different impact energies, such as 50J, 70J, and 100J, were applied to the specimen. Consequently, a maximum load of 5.5 kN occurred when the striker penetrated the upper face sheet in all experiments. The maximum load occurred at 4.2 ms for 50J, 3.5 ms for 70J, and 3.0 ms for 100J, indicating that the greater the impact energy was, the shorter the time was until the maximum load. After the maximum load occurred, that is, after the penetration of the upper face sheet, the striker penetrated 10 mm further, causing the core to be damaged in the 50J test, while the lower face sheet remained intact. In the 70J test, the striker penetrated the core and caused damage to the upper face sheet at 10 ms. Finally, in the 100J test, the striker penetrated both the upper face sheet and core and even the lower face sheet at 10 ms. Given the result above, the maximum load occurred when the striker penetrated the upper face sheet and the sandwich composite with aluminum foam core; the load then gradually decreased and then rapidly increased when the striker reached the lower face sheet, and the maximum load lasted slightly longer than the time required for the upper face sheet to be penetrated.