Research on Adaptability of Semi?rigid Material as Base Course for Long-life Asphalt Pavement
作者姓名:平树江  蒋亮  申爱琴  刘晓光
作者单位:1 Key Laboratory for Special Area Highway Engineering of Ministry of Education,Chang'an University,Xi'anShaanxi710064,China; 2 Binzhou Highway Administration Bureau,BinzhouShandong256614,China; 3 Tangshan Municipal Communications Bureau,TangshanHebei063000,China;  4 Zouping City Constructing Synthetic Development Co,Ltd,ZoupingShandong 256200,China
摘    要:In the light of semi?rigid material as base course for perpetual asphalt pavement,the bearing capacity and fatigue life of asphalt pavement with semi-rigid base cause and different asphalt layer's thickness were computed with BISAR30 after chosen typical pavement The impact of thickened layer on the stress of the semi?rigid base,the dry shrinkage and temperature shrinkages of the material were analyzed,and its adaptability as base for perpetual pavement was studied The result shows that (1) under the same load,with thickening of the asphalt layer,the compressive stress on the top and the tensile stress at the bottom of the semi?rigid base decrease obviously and the fatigue life of  the base increases substantially; (2)the impact of temperature and humidity on the  semi-rigid base is remarkably weakened,which leads to the fractures,erosion and reflecting cracks of the semi?rigid base to be controlled effectively

关 键 词:road engineering  semi?rigid base  crack  fatigue damage  long life  adaptability
收稿时间:2008-03-25
点击此处可从《公路交通科技》浏览原始摘要信息
点击此处可从《公路交通科技》下载全文
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号