| T91与钢102异种钢焊接接头氢致裂纹研究 |
| |
| 引用本文： | 史春元,索洪有.T91与钢102异种钢焊接接头氢致裂纹研究[J].大连交通大学学报,2001,22(1):83-86. |
| |
| 作者姓名： | 史春元 索洪有 |
| |
| 作者单位： | 1. 大连铁道学院材料科学与工程系
2. 大连铁道学院交通运输工程系 |
| |
| 摘 要： | 用甘油法分别测定了CM-9Cb、R347和国内新研制的T91专用焊条熔敷金属中的扩散氢含量.通过阴极电解渗氢和定载延迟开裂试验，研究了选用不同焊条焊接时，T91与钢102异种钢接头的氢致裂纹倾向，确定了临界启裂应力.
|
| 关 键 词： | 氢致裂纹 焊条 临界应力 |
| 文章编号： | 1000-1670(2001)01-0083-04 |
| 修稿时间： | 2000年12月20 |
Investigation of Hydrogen-induced Cracking on T91/Steel 102 Welded Joint |
| |
| SHI Chun-yuan,SUO Hong-you.Investigation of Hydrogen-induced Cracking on T91/Steel 102 Welded Joint[J].Journal of Dalian Jiaotong University,2001,22(1):83-86. |
| |
| Authors: | SHI Chun-yuan SUO Hong-you |
| |
| Abstract: | The diffusible hydrogen content in the deposited metal using CM-9Cb, R347 and newly-developed T91 electrode was measured respectively through glycerine hydrogen test, and the tendency for hydrogen-induced cracking of the T91 and steel 102 joint welded with different electrodes was investigated by means of electrolytic hydrogen charging and constant-load delayed cracking test, and the critical stress was determined. |
| |
| Keywords: | Hydrogen-induced cracking welded critical stress |