| 树脂基纳米涂层复合材料力学性能试验研究 | |
| 引用本文： | 许荔,江晓禹,钱林茂. 树脂基纳米涂层复合材料力学性能试验研究[J]. 西南交通大学学报, 2005, 40(3): 347-350 |
| 作者姓名： | 许荔 江晓禹 钱林茂 |
| 作者单位： | 1. 西南交通大学应用力学与工程系,四川,成都,610031 2. 西南交通大学机械工程学院,四川,成都,610031 |
| 基金项目： | 教育部优秀青年教师资助计划[2002]04;感谢西南交通大学基础科学研究基金资助（20011306）;感谢郑世瀛教授、邢建新老师、史新雨老师和朱昊昊教授对于试验的全力帮助. |
| 摘 要： | 用纳米划痕和纳米压痕试验对Al2O3短纤维增强环氧树脂复合材料基体涂覆纳米Al2O3涂层后的性能进行对比试验分析，研究涂层表面性能与涂层以及涂覆工艺的关系．环氧树脂固化的同时和固化后涂覆的涂层分别称为同时涂层和后期涂层．同时涂层和后期涂层使涂层的弹性模量从基体的1．0GPa分别提高到3．3～3．9MPa和2．1～4．0GPa；硬度从分别提高到700～1300MPa和400～600MPa． |
| 关 键 词： | 弹性模量 硬度 纳米涂层 纳米压痕试验 纳米划痕试验 Al2O3短纤维 环氧树脂 复合材料 |
| 文章编号： | 0258-2724（2005）03-0347-04 |
| 收稿时间： | 2004-03-01 |
| 修稿时间： | 2004-03-01 |
Experimental Investigation on Mechanical Properties of Nano-Al2O3 Coating on Resin Matrix Composites |
|
| XU Li,JIANG Xiao-yu,QIAN Lin-mao. Experimental Investigation on Mechanical Properties of Nano-Al2O3 Coating on Resin Matrix Composites[J]. Journal of Southwest Jiaotong University, 2005, 40(3): 347-350 | |
| Authors: | XU Li JIANG Xiao-yu QIAN Lin-mao |
| Affiliation: | 1. Dept. of Appl. Mechanics and Eng., Southwest Jiaotong University, Chengdu 610031, China; 2. School of Mechanical Eng. , Southwest Jiaotong University, Chengdu 610031, China |
| Abstract: | The mechanical properties of nano Al 2O 3 coating on Al 2O 3 short fiber reinforced epoxy composites were analyzed with nano indentation and nano scratch tests to study the relationship between the properties and coatings and coating procedures. The procedures to coat the coatings during and after the solidification of the epoxy were used. The former and latter procedures make the elastic modulus of the coatings increase from 1.0 GPa for the matrix to 3.3~3.9 GPa and 2.1~4.0 GPa, respectively, and the hardness of the coatings raise from 200 MPa for the matrix to 700~1 300 MPa and 400~600 MPa, respectively. |
| Keywords: | elastic modulus hardness nano-coating nano-indentation test nano-scratch test Al2O3 short fiber epoxy composites |