采胜氰化,渗硼复合工艺提高钢板压弯模具的使用寿命

采用氰化，渗硼复合工艺处理的钢板压弯模具其表面有一层白亮的Ｆｅ２Ｂ，次表层有近１ｍｍ厚的高Ｃ，Ｎ区淬火回火后形成回火马氏体，与Ｃ、Ｎ、Ｂ三元共渗的情况有很大差别，模具表明，采用该工艺处理后的模具，使用寿命可提高近２０倍。     

6V150型柴油机曲轴深层渗碳后高温回火工艺对淬火硬度的影响

分析了６Ｖ１５０型柴油机１８０ｒ２Ｎｉ４ＷＡ钢制曲轴层渗碳后高温回火工艺对淬火硬度的影响。该曲轴经深层渗碳后，渗碳层残余奥氏体较多几次回火可提高淬火后的表面硬度。５５０℃高温回火三次，淬火后的表面硬度最高。     

汽车离合器驱动盘扭转疲劳试验断裂原因分析

采用金相检验、化学分析、机械性能和硬度检验等方法对表面经碳氮共渗处理的STW22离合器驱动盘早期断裂原因进行分析。结果表明:材料成份不均匀及碳氮共渗淬回火工艺不当是导致离合器驱动盘过早开裂的主要原因,并提出了预防开裂的改进后淬火工艺。     

QPQ盐浴复合处理技术应用研究

应用无公害的ＱＰＱ盐浴复合处理技术，定性分析共渗层化素之素，着重分析了共渗层相组织的表面面硬度，研究了ＱＰＱ处理温度，时间对洪渗层深度，硬度的影响。     

稀土对30CrMnSiA钢离子S—N—C共渗组织和耐磨性能的影响

本文研究了稀土元素对离子硫、氮、碳共渗层金相组织，渗层深度及耐磨性能的影响。结果表明，一定量的稀土元素对离子硫、氮、碳工艺具有较明显的催渗作用，使渗层深度提高２５％以上，改善了表面组织，使表面硬度增强，耐磨性能提高２倍以上。     

铁基粉末冶金件的化学表面改性处理

化学表面改性处理的铁基粉末冶金件表面可获得比普通热处理更高的硬度、耐磨性和疲劳强度，同时心部保持良好的塑性和韧性。应尽量选择高密度粉末冶金材料。化学表面改性处理通常在气体介质炉中进行，温度、保温时间及气氛的控制很关键。一般首选渗碳处理。淬火和回火都影响零件的最终品质，在铁基粉末冶金材料中加入合金元素可提高其淬透性。可采用蒸汽处理、渗硫和碳氮共渗等不同方法来满足各种零件不同的使用功能。     

气门杆耐磨减摩钒氮硫共渗工艺及其摩擦学特性研究

针对发动机进排气门导杆采用ＱＰＱ类工艺处理的诸多弊端，在国家发明专利（８９１０８１２３．２）工艺的基础上，从盐浴成分配比、活性成分、热处理参数及共渗处理层的摩擦学性能等多方面对进行了研究。研究结果表明，适合气门导杆表面处理的ＴＮＤ－２工艺，即钒氮硫盐浴共渗技术，其渗层质量、摩擦学性能均优于现用于所门处理的几种工艺，且生产效率提高，污染降低。经该工艺处理的玉柴ＹＣ６１０５ＱＣ发动机气门顺利通过１００     

化学镀镍工艺在汽车节温器上的应用

采用化学镀镍工艺对汽车节温器表面进行处理，通过SEM分析了镀镍层表面的显微组织和相结构：采用HXZ-100显微硬度计测试了镀层的硬度；将镀镍层分别浸入10％NaCl溶液、10％HCl溶液和10％NaOH溶液中进行耐蚀性对比试验。结果表明，施镀40min后，镀层均匀、致密、无明显缺陷；在上述溶液中浸泡48h后，镀层无腐蚀孔出现；镀层在29．4N压力下研磨没有发生脱落，附着力极好。镀层综合性能完全满足汽车节温器产品的有关技术要求。     

稀土对硫氮碳共渗的影响及共渗层磨损特性及磨损机理的…

研究了稀土以墩子硫氮碳共渗及耐磨性的影响，探讨了稀土对离子硫氮碳共渗的催渗机理，试验结果表明：稀土对离子硫氮碳具有明显的催渗作用，可使渗层深度提高约２５％，硫化物层牢固，表面硬度提高且硬度梯度平缓，在不同的磨擦条件下，耐磨性均有不同程序的提高。     

G10CrNi3Mo渗碳淬火工艺探索

G10CrNi3Mo材料为渗碳轴承钢，用于制造尺寸较大的重要渗碳零件。该材料中含有大量的合金元素镍，经过常规的渗碳淬火热处理后，由于材料的MS点很低，表层为粗大的马氏体和大量的残余奥氏体组织（可达到6-7级），表面硬度仅为HRA78-80。零件即使在淬火后经过冰冷处理，也很难达到正常的硬度要求。通过采用带中间冷却的渗碳淬火工艺，较好的解决了上述问题，表面硬度可达到HRA81以上。     

Application of the reverse 3D scanning method to evaluate the wear of forging tools divided on two selected areas

This study is focused on tools used in the industrial hot forging process of a front wheel forging (eventually–gear wheel) manufactured for the automotive industry. Four different variants were applied for the tools: 2 die inserts were coated with two different hybrid layers (GN + PVD type), i.e. AlCrTiN and AlCrTiSiN, one insert was only nitrided, and one was pad welded, to improve tool durability. The tool wear was analysed and represented by the material degradation on the working surface, based on the 3D scanning and the material growth of the periodically collected forgings. Additionally, the scanned tools were divided into two areas, in which it was found, based on the reliminary analysis, that various degradation mechanisms are predominant. Microstructural and hardness measurements of the analyzed tools were also performed. Based on the results, it was found that, in the central part of the die insert (area A), thermo-mechanical fatigue and wear occurred, while in the area of the bridge insert (area B), only abrasive wear could be observed. For these areas (A and B), the loss of material was determined separately. In area A for the inserts with hybrid layer GN+AlCrTiSiN and gas nitrided, an intensive increase of wear took place, which was not observed for the pad welded and GN+AlCrTiN layer insert, for which, together with the increase of the forging number, a proportional growth of the loss of material occurred. In area B the weakest results were obtained for the insert with GN+AlCrTiSiN layer, while wear of other die inserts grew similar and proportional.     

利用喷丸硬化提高渗碳齿轮的强度

研究表明，采用喷丸硬化工艺是一种改善渗碳材料表面异常的有效方法，可以显著提高渗碳齿轮的疲劳强度，介绍了日本ＩＳＵＳＺＵ汽车研究中心在汽车齿轮上应用喷丸硬化工艺的情况，并重点介绍了喷丸硬化的处理效果和工艺方法。     

高速公路隧道水泥混凝土路面抗滑能力恢复技术的应用

隧道水泥混凝土路面的抗滑能力直接关系着隧道的行车安全,抗滑能力恢复是隧道水泥混凝土路面运营需要面对的普遍问题。结合工程案例,针对运营隧道水泥混凝土路面的抗滑处治,介绍铣刨刻槽、HOG表面纹理化技术、铝矾土抗滑表层等3种抗滑能力恢复技术的关键技术参数、工艺流程及处治效果,以期为其他隧道水泥混凝土路面抗滑处治提供借鉴。     

基于Redis盾构远程监控系统设计

为解决B/S模式的盾构远程监控系统随着处理数据量加大出现数据库负载过大、网页显示延迟等问题,基于B/S模式和Redis缓存技术设计盾构远程监控系统,系统包括数据层、应用层和展示层3部分。在数据层中使用Redis缓存数据,使系统具有高效的数据处理能力,并搭建Redis集群以实现高容灾和高可用性; 应用层和展示层采用分模块方式设计,可降低系统耦合度,简化开发流程。     

STRATA技术在路面防反射裂缝中的应用研究

针对引进不久的STRATA技术，结合汉（武汉）宜（宜昌）高速公路沥青加铺工程，从旧水泥混凝土路面的综合处治、STRATA应力吸收层的混合料设计、施工工艺、施工中日常检测几个方面对STRATA技术的应用进行了全面研究，并肯定了其在水泥混凝土路面加铺沥青混凝土面层时的防反射裂缝作用。     

耐磨复合材料强化及快速翻制铸造模具

铸造中如何采用成本低、加工周期短、维修方便复合材料模具及强化模具的表面技术，可极大地提高经济效益，本通过对铸造模具表面强化原理的分析，着重于对高耐磨复合材料的研究，介绍了耐磨材料的组成，结构，并以生产中的应用实例介绍了耐磨材料在实际模具铸造中的应用。     

氧化铜无机粘结剂的应用

从粘结剂的配制、粘结剂的粘结性能及粘结工艺等几个方面，介绍了氧化铜无机粘结剂及其在机械行业特别是在模具制造中的应用。     

康明斯6B柴油机曲轴的模锻

介绍了康明斯６Ｂ柴油机曲轴在锻压机上的曲面分模直接模锻成型工艺。对工艺方案的确定及锻模设计中的一些关键问题进行了分析，应用该模锻工艺和模具，已累主地生产康明斯６Ｂ柴油机轴锻件２万多件，替代了进口，保证了康明斯发动机国产化对曲轴锻件的需求。     

金属路面加筋网防治反射裂缝试验与应用分析

使用金属路面加筋网防治半刚性基层裂缝反射到沥青面层,是在基层和面层之间铺设并固定一层金属路面加筋网,其上铺设沥青面层,最后碾压成形。该技术在国外属于成熟技术,近年来在我国修建了试验路,取得了预期效果。     

轿车连杆精密辊锻-模锻复合锻造工艺

针对轿车连杆锻件的特点、技术条件与要求，提出一种精密辊锻-液压模锻锤模锻复合工艺，并进行了精密锻造工艺设计及模具设计。以广州本田轿车连杆体精密锻造成型为例，进行了精密辊锻制坯-液压模锻锤模锻复合工艺研究。研究结果表明，采用此工艺生产轿车连杆件，产品质量高，生产稳定可靠，比传统锤上模锻工艺节约原材料15％以上，能耗降低60％，锻件成本降低10％。