The effects of Ca element on the microstructure and mechanical properties of AZ61-1.2Y alloy were investigated by microstructure observation, tensile tests and fracture analysis. The results show that, with the addition of Ca element, the microstructure of AZ61-1.2Y was obviously refined, high melting point Al2Ca intermetallic compound formed, and β-Mg17Al12 phase disappeared. With 1.0% Ca addition, the values of tensile strength at 25, 150 and 175 ℃ reached their maxima simultaneously, 225, 182, and 175 MP...     

闭孔泡沫铝与铝及铝合金覆板的冶金结合

利用直接冶金结合方法,研究了铝及铝合金覆板的厚度及复合温度与时间对闭孔泡沫铝夹心三明治与覆板结合层厚度的影响.利用金相显微镜观察了泡沫铝夹心与覆板结合界面的微观组织,并测量了结合界面的扩散层厚度和显微硬度.研究结果表明,铝熔体与纯铝和铝合金覆板复合温度越高,复合时间越长,他们之间的扩散层厚度越大;当纯铝板的预热温度为400~450℃,复合速度为53.9~74.4 mm/min时,泡沫铝夹芯与纯铝板形成良好冶金结合,复合界面的互扩散层厚度为39~44μm;当铝合金覆板的预热温度为240℃,复合速度为58.3 mm/min时,制备铝合金覆板泡沫铝三明治所需的铝合金板最小厚度应为7.9 mm.     

碳纤维增强铝基复合材料的制备及其拉伸性能

利用挤压铸造方法,采用三种不同的凝固条件,制备了连续长碳纤维增强铝基复合材料的拉伸试样,并对其拉伸性能进行了试验。试验结果表明,该复合材料的抗拉强度和弹性模量皆随碳纤维的体积含量增加而增加。含48％碳纤维的复合材料比基体材料的拉伸强度高50％以上,但塑性指标随碳纤维含量的增加而显降低,当连续碳纤维的体积含量较小时,凝固条件对该复合材料的抗拉强度影响较大,对弹性模量的影响较小;当碳纤维的体积含量较大时,凝固条件对该复合材料的抗拉强度影响较小,而对弹性模量的影响较大。     

碳纤维增强铝基复合材料的制备及其拉伸性能

利用挤压铸造方法,采用三种不同的凝固条件,制备了连续长碳纤维增强铝基复合材料的拉伸试样,并对其拉伸性能进行了试验．试验结果表明,该复合材料的抗拉强度和弹性模量皆随碳纤维的体积含量增加而增加．含48％碳纤维的复合材料比基体材料的拉伸强度高50％以上．但塑性指标随碳纤维含量的增加而显著降低．当连续碳纤维的体积含量较小时,凝固条件对该复合材料的抗拉强度影响较大,对弹性模量的影响较小;当碳纤维的体积含量较大时,凝固条件对该复合材料的抗拉强度影响较小,而对弹性模量的影响较大．     

X射线衍射法测试高速列车车体铝合金残余应力

为了准确、无损、快速地检测高速列车铝合金的表面残余应力,采用等强杆拉伸试验方法,用X射线衍射法对测试结果进行标定,并用X射线衍射法、盲孔法以及有限元法对测得的车体铝合金焊接接头残余应力进行了对比.结果表明:等强杆拉伸试验标定过程中,在10～70 MPa范围内,随着拉伸载荷的增加,X射线法测得的应力与载荷应力具有一致性,可采用X射线衍射法对车体关键部位应力状态进行测试分析,X射线衍射法残余应力的数值略大于理论计算值和电测法计算值;车顶铝合金焊接接头最大残余应力可达146.3 MPa;X射线衍射法与等强杆标定方法、盲孔法、有限元计算模拟方法的残余应力结果保持了较好的一致性.     

AZ31B镁合金电子束焊接接头显微组织及疲劳性能

为了改善镁合金焊接接头的微观组织及其力学性能,采用真空电子束焊接工艺对厚10 mm的AZ31B镁合金板材进行焊接,分析电子束对接接头的显微组织、元素分布和物相组成,检测了电子束对接接头静载拉伸性能和疲劳性能.试验结果表明AZ31B镁合金电子束焊接接头的微观组织和力学性能均得到了改善:焊缝区晶粒明显细化,焊缝区Mg、Zn元素的质量分数分别降低了0.12%和0.28%,Al、Mn元素的质量分数分别增加了0.24%、0.14%,焊缝区为单相α-Mg,无明显的低熔点β-Mg17Al12脆性;焊接接头的抗拉强度为242 MPa,能够达到母材的抗拉强度;在脉动载荷（R=0.1）、2×106循环次数下,其接头的疲劳强度为91 MPa,能达到母材的78.4%.      

闭孔泡沫铝的孔隙结构及压缩变形过程研究

为研究压缩空气法制备的闭孔泡沫铝的孔隙结构对其力学性能的影响和压缩变形过程,测量了不同密度泡沫铝的孔隙结构参数,分析了孔径与密度关系,并通过单向压缩实验,分析了密度对破碎压力和杨氏模量的影响以及裂纹产生与扩展情况.研究结果表明：泡沫铝的孔径与密度的关系为ρ＊=0.108 5＋4.862 7exp（-0.608Φ）.在单向压缩时,随着压缩载荷的增加,孔壁在弹性变形后产生弯曲,裂纹首先在应力集中的缺陷处和孔壁强度低的位置产生向次薄弱的孔壁扩展.应力水平越高,裂纹扩展越快;当孔的壁面上存在强度差异时产生褶皱;裂纹贯穿孔壁后发生失稳断裂并可能发生转动,并导致塑性坍塌;应变继续增加,孔穴破碎进入致密化过程.     

铸造多孔铝的吸声性能与应用

多孔铝是一种新型的多用途金属材料,本文介绍了铸造多孔铝合金两种常用的制备方法,分析了孔径和孔隙率对吸声性能的影响及多孔铝合金在吸声、减震方面的应用。     

Purification effects of C2Cl6 on A00 aluminum

The effects of several fluxes on purification, microstructures and properties of A00 aluminum have been studied. The experimental results and analyses indicate that many cracks and large porosities exist in the surface film above the melt purified by C₂Cl₆ and that the film is floc and mostly composed of Al₂O₃ and pure aluminum, which carries many carbon particles and AlCl₃ not fully volatilized. And then over 50% (mass fraction) of the all-melting residue is pure aluminum, which is one of the major reasons for high melting loss. Moreover, because of a mass of gas bubbles and a state of seethe, there are many inclusions which size is under 10 ??m in the microstructure of A00 aluminum purified with C₂Cl₆ or fluxes containing C₂Cl₆. With this purifying method, the aluminum crystal grains are extended along the radius that was observed firstly and the average crystal size of A00 aluminum are about 100?C150 ??m. In addition, small size inclusions have little affected on tensile strength and micro inclusions under 10 ??m have little affected on elongation.     

WELDOX960E高强钢手工电弧焊焊接接头组织与力学性能

通过拉伸、弯曲、冲击、硬度和金相组织分析等试验,对手工电弧焊焊接WELDOX960E高强钢焊接接头组织和力学性能进行研究.研究结果表明：采用Phoenix SH Ni2 K130焊条、手工电弧焊焊接WELDOX960E高强钢时,可以获得拉伸、弯曲、冲击性能良好的接头;其焊缝组织为针状铁素体与粒状贝氏体的混合分布;熔合区及粗晶区组织为板条马氏体和少量白色M-A块区;正火区组织为块状铁素体、粒状贝氏体和珠光体;母材显微组织为回火索氏体;WELDOX960E高强钢焊缝硬度为270 ～ 300 HV,且距离熔合线30 mm处出现软化区.     

高铝锌基合金拉伸断裂特征的研究

对高铝锌基ＺＡ２７合金在室温下的拉伸断裂特征进行了研究,结果表明,ＺＡ２７合金在拉应力作用下,其裂纹源始于树枝晶间的α＋η共晶组织,裂纹扩展过程是以沿α＋η,剪断树枝状α相和ε相的方式进行的,并探讨了ＺＡ２７中各相对其强度和塑性的影响。     

Microstructures and mechanical properties of various Mg-Li wrought alloys

Three kinds of ultra-light Mg-Li wrought alloys,Mg-5.5Li-3Al-1Zn-1Ce,Mg-7.0Li-3Al-1Zn-1Ce and Mg-10.5Li-3Al-1Zn-1Ce,were prepared by vacuum induction melting furnace;then the alloys were extruded and rolled.The microstructures and properties of these alloys were studied.The results indicate that the Mg-5.5Li3Al-1Zn-1Ce alloy has the highest strength,the Mg-10.5Li-3Al-1Zn-1Ce alloy has maximum elongation,and the Mg-7.0Li-3Al-1Zn-1Ce alloy has good comprehensive performance.Rolling deformation can increase strength further after extrusion deformation.     

发泡工艺参数对铝熔体泡沫生成量的影响

利用空气发泡法研究发泡温度、入射气体压力和流量以及吹气头往复运动频率对铝熔体泡沫生成量和熔体表面气泡尺寸的影响,分析了气泡尺寸对其内部气体压强和发泡工艺参数对铝熔体泡沫生成量的影响．研究结果表明,铝熔体泡沫生成量随射入空气P1V1值的增大而增加．当P1V1从5．7MPa·cm^3／min增加到7．2MPa·cm^3／min,铝熔体表面的气泡半径尺寸由6．93mm增加到7．46mm,铝熔体泡沫的生成率从3210cm^3／min增加到4400cm^3／min．当入射气体P1V1为5．67MPa·cm^3／min时,发泡温度由620℃升高到640℃,气泡半径由3．57mm增大到3,66min,泡沫生成量由288g增大到2978cm^3／min．     

发泡工艺参数对铝熔体泡沫生成量的影响

利用空气发泡法研究发泡温度、入射气体压力和流量以及吹气头往复运动频率对铝熔体泡沫生成量和熔体表面气泡尺寸的影响,分析了气泡尺寸对其内部气体压强和发泡工艺参数对铝熔体泡沫生成量的影响.研究结果表明,铝熔体泡沫生成量随射入空气P1V1值的增大而增加.当P1V1从5.7 MPa·cm3/min增加到7.2 MPa·cm3/min,铝熔体表面的气泡半径尺寸由6.93 mm增加到7.46 mm,铝熔体泡沫的生成率从3 210 cm3/min增加到4400 cm3/min.当入射气体P1V1为5.67 MPa·cm3/min时,发泡温度由620℃升高到640℃,气泡半径由3.57 mm增大到3.66 mm,泡沫生成量由288 g增大到2 978 cm3/min.     

服役温度对BFRP/铝合金粘接接头静态失效的影响

在车辆轻量化设计过程中, 为了预测BFRP/铝合金粘接接头在服役温度下的静态失效行为, 加工了处于拉应力、剪应力与拉剪组合应力状态的粘接接头, 根据车辆服役温度特点, 选取-40℃、-10℃、20℃、50℃、80℃五个温度测点, 通过准静态拉伸试验, 得到不同应力状态下接头失效强度随温度的变化规律, 分析了粘接接头失效形式和失效准则; 基于粘接接头在不同温度下的拉、剪应力, 建立了接头的二次应力失效准则方程, 对不同温度下的接头强度进行失效预测。分析结果表明: 粘接接头的失效强度受温度的影响明显, 随温度升高, 失效强度减小; 粘接接头中剪应力和拉应力的不同占比也会对接头失效强度造成一定的影响, 随着剪应力比例增大, 温度升高使接头失效强度下降更明显; 相比于低温-40℃, 高温80℃时的拉伸接头与剪切接头失效强度的下降幅度分别为47.77%与61.49%;随着温度升高, 粘接剂的失效应力和杨氏模量逐渐减小, 而失效应变逐渐增大, 说明温度很大程度上影响了粘接剂的力学性能; 粘接接头失效形式为内聚和纤维撕裂的混合失效, 拉应力作用下接头更容易发生纤维撕裂, 并且随温度升高, 纤维撕裂面积减小, 因此, 为了防止纤维撕裂, 需要避免粘接接头受拉应力作用; 粘接接头在不同温度下的二次应力失效准则曲线拟合精度均在0.957以上, 并绘制了失效准则响应曲面, 直观反映了粘接接头失效强度在车辆服役温度下的变化规律。      

胶粘剂和CFRP吸湿对复合材料粘接接头失效的影响

对胶粘剂和复合材料的影响进行解耦;采用常温环境分别对胶粘剂、碳纤维增强树脂基复合材料(CFRP)和CFRP/铝合金粘接接头进行不同时间周期的浸泡,研究了不同应力状态对粘接接头失效的影响;以准静态失效测试的失效强度和失效模式分析为主,结合傅里叶变换红外光谱仪分析、差示扫描量热法分析和扫描电子显微镜分析,分别研究胶粘剂和CFRP吸湿后的失效机理,揭示了吸湿对复合材料粘接接头失效的影响机理。分析结果表明:胶粘剂在吸湿30 d后发生了水解,失效强度下降约53.7%,失效应变约为原来的3.2倍;CFRP吸湿后表面粘附性降低,容易引起界面失效,但打磨之后能够得到改善,CFRP吸湿后纤维/基体界面力学性能降低,在正应力状态下更容易造成纤维撕裂;CFRP/铝合金粘接接头的失效强度在吸湿30 d后下降了约23%,失效断面中胶粘剂出现了韧性断裂和界面失效;通过对胶粘剂、CFRP和CFRP/铝合金粘接接头吸湿后的失效分析,发现剪应力状态下的CFRP/铝合金粘接接头失效主要受胶粘剂吸湿后的性能下降影响,其次是界面失效的影响,而正应力状态下的CFRP/铝合金粘接接头失效还受CFRP性能下降造成的纤维撕裂影响。      

过共晶铝硅合金变质工艺研究

本文研究了P、RE、S单独加入及P-RE、P-S、P-Na联合加入对Al-20％Si合金的变质作用，比较了各自的变质效果。考察了联合变质的最佳变质温度及联合变质长效性。结果表明，P-RE、P-S联合变质具有较好的双重变质效果，联合变质后合金机械性能有较大的提高。最佳变质温度为840℃左右，变质效果至少可持续3h.     

LY12铝合金搅拌摩擦焊工艺研究

对LY12铝合金进行了搅拌摩擦焊接工艺试验,并对焊接接头进行了金相观察和力学性能检测.试验结果表明,合理的焊接参数匹配是取得性能优良焊接接头的前提.当旋转速度为905 r/min、焊接速度为33.6 mm/min、肩部压力为48 MPa时施焊,可获得成型良好无缺陷焊接接头,且焊缝区晶粒细小.搅拌摩擦焊焊接轧态LY12铝合金时,焊接时的热输入可部分消除接头处金属的冷作硬化.随着焊接速度的提高,焊接热输入量降低,消除冷作硬化的能力减弱,焊接接头抗拉强度提高.     

LY12铝合金搅拌摩擦焊工艺研究

对LY12铝合金进行了搅拌摩擦焊接工艺试验,并对焊接接头进行了金相观察和力学性能检测.试验结果表明,合理的焊接参数匹配是取得性能优良焊接接头的前提.当旋转速度为905 r/m in、焊接速度为33.6 mm/m in、肩部压力为48MPa时施焊,可获得成型良好无缺陷焊接接头,且焊缝区晶粒细小.搅拌摩擦焊焊接轧态LY12铝合金时,焊接时的热输入可部分消除接头处金属的冷作硬化.随着焊接速度的提高,焊接热输入量降低,消除冷作硬化的能力减弱,焊接接头抗拉强度提高.     

泡沫铝压缩试验及等效仿真模型研究

为了研究泡沫铝结构在直升机耐坠性设计中的应用效果,本文基于万能材料试验机和霍普金森压杆分别对两种相对密度的闭孔泡沫铝在准静态（0.001/s）和高应变率下（500/s、1 000/s）的力学性能进行了测试;然后,建立了可反映应变率效应的泡沫铝等效有限元模型;最后,将泡沫铝等效模型应用于直升机驾驶舱耐坠性的仿真中,分析了置入不同密度泡沫铝等效模型后直升机受到的冲击和变形情况.结果表明：泡沫铝的平台应力以及质量比吸能随相对密度、应变率的增加而增加,但密实化应变则相反;泡沫铝等效有限元模型与实验结果曲线保持一致,模型准确性较高;此外,通过置入两种密度的泡沫铝材料,驾驶舱地板的最大变形量分别减少了28%和73%,机身部件的承载压力平均减少了28%和42%,高密度泡沫铝承载能力更强,效果更好.