11.0 L柴油发动机气门弹簧断裂分析及优化措施

采用形貌观察、显微组织检验、硬度检验等方法,对发动机气门弹簧进行综合试验,分析弹簧断裂的原因。结果表明：弹簧经绕制后,内圈表面存在较大张应力,若回火不充分会造成内圈形成过大残余张应力,容易导致弹簧内圈开裂。为此,采用 150 000 Hz高频感应淬火,并通过抛丸强化表面,将残余张应力转化为残余压应力,以提高气门弹簧的疲劳寿命及载荷能力,有效解决气门弹簧断裂问题。     

单面双槽钢板弹簧在汽车上的应用

单面双槽钢板弹簧用在汽车悬挂上,比一般平扁钢制的弹簧要优越得多. 钢板开槽后,打破了原来的应力分布对称状态.使拉应力减小、压应力增大.不仅改善了结构强度,提高了承载能力,而且还延长了疲劳寿命.单片对比约35%;总成达15～20万公里. 文中还详细介绍了这种钢板弹簧的设计方法、制造工艺、道路试验和使用情况.     

凿岩台车伸缩臂材料的疲劳寿命研究

本文研究了凿岩台车伸缩臂材料在拉-拉或拉-压疲劳试验过程中平均应力与疲劳极限之间的关系。根据疲劳极限值导出等效理论疲劳极限与应力疲劳寿命估算公式,并通过引入频率因子对疲劳寿命公式进行修正,推出伸缩臂材料在不同频率条件下的应力疲劳寿命公式,并进行了试验验证。     

拉-压交变荷载下沥青混合料的疲劳性能

为了研究交变力学状态下沥青混合料的疲劳性能,开发专用加载设备,选择AC-25F和AC-16C两种材料作为研究对象,进行不同荷载级别和不同应力比下的疲劳试验,分析荷载级别和压应变对沥青混合料疲劳行为的影响,并建立考虑压应力影响的疲劳预估模型.结果表明:各种应力比下,沥青混合料疲劳寿命与拉应力呈对数线性关系,但压应力显著延长了材料的疲劳寿命.对于AC-25F,其在应力比为-0.5,-0.3,-0.1时的疲劳寿命分别为应力比0.1时的2.52倍、1.53倍和1.03倍;对于AC-16C,相应的疲劳寿命则分别为应力比0.1时的4.90倍、3.31倍和2.30倍;所建立的考虑压应力影响的疲劳预估模型可有效弥补现有模型仅考虑拉应力作用的缺陷,为路面结构设计和疲劳预估提供参考.     

55SiMnVB单面双槽断面弹簧

二汽的三种基本车型(EQ140,EQ240EQ245),及其变形车的钢板弹簧,均选用了55SiMnVB新材料轧制的单面双槽型钢,并在设计,工艺上采取了有效措施,使得该产品在性能,使用寿命以及重量指标等方面均达到较好的效果。一、在设计方面 1.适当增大弹簧的长度,选择合适的片厚使钢板弹簧的比应力明显下降,这对提高弹簧的疲劳寿命起了一定的作用。适当减小刚度可使偏频降低,从而提高汽车的平顺性,表1列出EQ140(单面双槽断面)。EQ140(矩形断面)CA10的对比数据,表中应力均为拉应力。     

基于名义应力法的疲劳卡片构建方法研究

基于有限元的疲劳寿命预测可应用于各行业,疲劳寿命预测精度的提高,离不开有效的材料疲劳卡片,疲劳卡片反映了载荷水平与疲劳寿命的关系。通过设计合理的材料试样的疲劳试验,结合试验与有限元计算,计算不同损伤参量创建应用于疲劳寿命分析的材料疲劳卡片,同时对疲劳卡片的仿真精度进行了验证。结果表明,基于名义应力法构建的疲劳卡片具备较高的预测精度,结合材料试验数据与仿真结果构建的多应力比S-N疲劳卡片,可用于其他适用于应力疲劳分析的零部件疲劳寿命分析,为提高零部件疲劳寿命预测精度提供新的技术途径,为零件的前期结构设计提供参考,可在不同领域进行推广并开展进一步分析研究。     

发动机罩盖锁体弹簧断裂分析

从断口、材料检测及应力分析三个方面对过早失效的发动机罩盖锁体弹簧进行分析研究,明确失效原因并提出相应的改进措施。研究结果显示,弹簧过早地断裂失效是由于工作载荷过大所导致。通过增加圈数、减少钩环半径等办法对弹簧进行改进,可降低工作应力、提高弹簧疲劳寿命。改进后,产品达到了测试要求。     

汽车发动机气门弹簧残余应力的研究

根据气门弹簧失效机理和气门弹簧的应力分析,阐述了与钢丝轴线呈45°(或135°)方向的残余应力是直接影响气门弹簧疲劳性能的因素。采用X射线应力测试仪对去应力退火和喷丸强化处理两道关键工序中弹簧的内、外圈表面和不同喷丸强化处理参数下次表面的残余应力进行了试验,并对气门弹簧进行了模拟发动机实际工况疲劳试验验证,得到了气门弹簧在这两道关键工序中残余应力和疲劳性能的关系,为今后通过优化工艺来改善气门弹簧的疲劳寿命和性能奠定基础。     

浅析重型汽车钢板弹簧台架疲劳寿命的影响因素

1前言 钢板弹簧是车辆悬架系统的重要部件之一,其产品的性能和质量特别是疲劳寿命直接关系到车辆行驶的安全性.本文通过一组试验数据试分析影响重型汽车钢板弹簧台架疲劳寿命的主要因素,给出提高疲劳寿命的方法. 2影响重型汽车钢板弹簧疲劳寿命的主要因素 按照GB/T 19844-2005《钢板弹簧》的规范要求,对材料为50CrVA的5架同型号钢板弹簧进行了性能和疲劳次数试验,试验数据见表1.     

随机载荷下汽车钢板弹簧疲劳设计方法

以路面不平度随机激励为输入，以钢板弹簧随机疲劳寿命估算为基础，对钢板弹簧的随机应力过程做了较深和的研究，最终提出了一种新的钢板弹簧参数设计方法。     

由PLC电控系统控制的液压卷耳机

由ＰＬＣ电控系统控制的Ｈ１６０／２５液压卷耳机是在引进英国ＦＢ公司的卷耳机样品的基础上发展的经有手动和半自动两种工作方式。该机的工作原理是将加热的弹簧钢板绕芯轴卷制，从而形成卷耳或包耳。该机是一机多用，它集切头－卷耳－成型于一体，可卷制平耳，垂耳及包耳。     

Effects of end coils on the natural frequency of automotive engine valve springs

In this paper, we present a method for estimating the natural frequencies of various engine valve springs such as constant pitch, two-step variable pitch, three-step variable pitch, and progressive springs. Since a valve spring’s surging amplitude is magnified when the spring’s natural frequency coincides with the frequency of the cam profile harmonic components, estimating the natural frequency of the spring is the first step in predicting valve spring surging phenomena. A new method for calculating the valve spring’s natural frequency is proposed in this paper that considers the end coil effect. This method predicts not only the natural frequency of a helical spring at a fixed number of active turns, but also the change in the natural frequency as the spring is compressed. The experimental results demonstrate that nonlinear characteristics of engine valve springs can be predicted from the given initial pitch curves.     

盾构主驱动密封失效检测及原因分析

为解决盾构主驱动密封系统在掘进过程中失效，造成主驱动、主轴承或齿轮损坏的问题，以某系列土压平衡盾构主驱动密封系统的结构和工作原理为基础，首先，采用适用于现场施工条件的主驱动密封气压检测技术，即分别向内、外密封各腔体内通入100 kPa压缩空气，保压30 min后，压降值在允许范围内为合格，超出为不合格，进而判定主驱动密封是否失效。然后，结合现场经验和理论分析，从设计、装配、操作、磨损4个方面对密封失效的原因进行分析，得出装配不合格、操作不当和正常磨损等问题均是目前最常见的密封失效原因。最后，针对密封失效原因，分别从设计、安装、操作、日常维保等各个环节进行预防把控，以保证主驱动密封系统达到设计使用寿命。     

Influential factors for HLA pump up in a roller finger follower engine

In an HLA (hydraulic lash adjuster) piston engine, “pump up” can occur when a valve is opened by the HLA when it should be closed. HLA pump up is more frequently encountered with exhaust valves than with intake valves. When HLA pump up in occurs in the exhaust valve, exhaust gas from the exhaust manifold enters the cylinder on the intake stroke, and fresh air-fuel mixture exits through the exhaust manifold on the compression stroke and is burned in the catalyst, causing partial burning, misfire, catalyst melting and power drop. HLA pump up occurs when the force on the valve from the HLA is higher than the force on the HLA from the valve. HLA pump up is related to design parameters, such as oil pressure, rocker ratio, spring load, spring surge, and both intake and exhaust valve timing. In this study, valve lift and load on a roller finger follower were measured at varying engine firing conditions to evaluate HLA pump up. The results indicated that effective measures to reduce HLA pump up include a higher rocker ratio, a lower oil supply pressure to the HLA, a higher spring installation load and a lower spring surge.     

EQ140型汽车空气压缩机气阀的改进设计

在分析和试验的基础上，从扩大气流通面积，改变阀片形状和厚度，改变阀片弹簧形状和刚度，以及减小余隙容积等方面，对ＥＱ１４０型汽车空气压缩机气阀进行了改进设计，对比试验表明，改进设计后，该空气压缩机的充气系数明显提高，较好的解决ＥＱ１４０型汽车窍压缩机泵气不足的问题。     

喷油器的改进对球型燃烧室柴油机排放的影响

通过减小喷油器针阀、弹簧座和弹簧等运动件的质量 ,达到减小喷油器运动惯量的目的 ;通过减小压力室直径 ,达到减小压力室容积的目的。最后将带有新设计的低惯量小压力室喷油器的柴油机进行排放性能测试 ,结果表明柴油机排放得到了改善 ,从而证实了这种方法的有效性     

Development of a valve and optimization of a tube for self-inflating tire

Worldwide, the tire market requires safe and eco-friendly tires. In this study, a self-inflating tire (SIT) was studied and manufactured. Self-inflating tire refers to a technique for maintaining appropriate tire pressure. An internal regulator senses when tire inflation pressure has dropped below the set air pressure. The tire boosts air through the valve when rolling and compressed air enters into the tire. This procedure keeps the tire air pressure at an appropriate level and increases tire safety. In this study, a regulator was used as a negative-pressure system. A check valve was selected the minute flow check valve depending on the shape of the configured system. In addition, the material of the tube was developed with excellent physical properties and resistances (elastic rebound, working temperature, etc.) owing to its complete compression and restoration. A tube performance tester was developed and a computer aided engineering (CAE) model was modeled for comparison with the test results. Using the tester and model, it was possible to optimize the shape of the tube and regulator. Finally, the reliability of the study was verified through the prototype test. The developed equipment and systems can be used for the manufacture of high-performance and safe tires.     

油气弹簧阀片厚度与节流缝隙的分析研究

利用节流阀片弯曲变形量Gr计算方法,对节流缝隙增量和弯曲变形量的关系进行了分析,对节流缝隙增量随压力的变化进行了探讨。对油气弹簧节流阀的设计进行了研究,给出了由车辆的基本参数设计节流阀片厚度和节流缝隙的方法和步骤,最后对所设计油气弹簧进行了阻力特性试验。     

少片变截面弹簧设计最大应力点的选择

从板簧设计等应力梁的概念出发,深入讨论了少片变截面弹簧的变截面设计方法,通过讨论弹簧设计比例尺效应问题,比较最大应力点在不同位置时的应力特点,提出了少片簧设计要充分考虑制造工艺的因素,根据变截面弹簧的片长和片厚选择合适的轧制斜率,把最大应力点放在弹簧根部的设计思想。     

二重管旋喷工法成桩直径实用计算方法

为了解决二重管旋喷工法成桩直径的预测问题，通过对二重管法成桩过程的理论分析，建立了可以考虑压缩空气影响的二重管法成桩直径的计算方法，并给出了相应的详细计算步骤。二重管法施工期间，压缩空气包裹高压水泥浆射流可以有效降低射流速度沿喷射距离的衰减速率，增强高压射流对土体的切削效应，使得高压旋喷桩的成桩直径明显增加，提高旋喷工法对软土地基的加固效果。所提出的实用计算方法可以有效考虑土性参数、旋喷参数以及压缩空气的影响。以旋喷施工时的空气喷射压力为主要控制参数，通过回归分析提出了可以表达压缩空气对成桩直径增大效应的定量计算公式。针对二重管法施工中压缩空气的常用压力范围0.5~1.5 MPa，得到了压缩空气包裹高压射流对旋喷桩成桩直径的增大比例，为27%~81%，这与工程实践经验非常接近（一般压缩空气可以提升桩径的范围为30%~90%）。以温州深厚软土地区的二重管法工程实例为依托，根据旋喷施工参数与土性参数，采用所提出的计算方法与成桩直径的现场实测结果进行了对比分析。分析结果表明：对于2根试桩C1和C2（实测直径分别为1.08，1.12 m），应用所提出计算方法产生的相对误差分别为5.6%和6.3%（计算直径分别为1.02，1.05 m），由此可见所提方法可以满足工程设计与施工的要求。