溶胶-凝胶法制备软磁纳米材料Fe2O3

首次采用添加分散剂溶胶-凝胶法制备软磁纳米材料Fe2O3,采取添加分散剂和改变焙烧方法保证晶粒尺寸.实验结果表明:软磁纳米晶制备中添加分散剂尿素,然后在高温(600℃)焙烧前增加一个低温(400℃)退火阶段,两项措施能保证Fe2O3原始晶粒尺寸在30～40nm.试验操作简单、过程易于控制、产品质量稳定.     

溶胶—凝胶法制备氧化铝薄膜

以异丙醇铝为原料，研究了溶胶的浓度、粘度及加入电解质的种类，电解质的浓度和焙烧温度等条件对成膜的影响。     

溶胶－凝胶法制备氧化铝薄膜

以异丙醇铝为原料，研究了溶胶的浓度、粘度及加入电解质的种类，电解质的浓度和焙烧温度等条件对成膜的影响．     

Fe32Mn3Al8Cr反铁磁精密电阻合金Al2O3防护涂层的研究

用溶胶-凝胶法在Fe32Mn3Al8Cr反铁磁精密电阻合金表面提拉制备Al2O3耐腐蚀防护涂层.采用X射线衍射分析涂层相结构,扫描电镜观察涂层表面形貌.在Fe32Mn3Al8Cr合金表面形成连续、光滑的Al2O3涂层,具有(110)择优取向的γ-Al2O3结构.采用动电位阳极极化法测定涂层的电化学腐蚀性能表明,与原始合金相比较,在1mol/L Na2SO4溶液中,Al2O3涂层的自腐蚀电位提高了571mV,自腐蚀电流密度降低了1个数量级以上,维钝电流密度降低了近1个数量级;在1%NaCl溶液中,自腐蚀电位与原始合金相当,自腐蚀电流密度降低了2个数量级,腐蚀电位高达2000mV(SCE)时仍未发生孔蚀击穿.而且,Al2O3防护涂层的耐均匀腐蚀和耐孔蚀性能均优于1Cr18Ni9Ti奥氏体钢.     

Fe32Mn3A18Cr反铁磁精密电阻合金Al2O3防护涂层的研究

用溶胶-凝胶法在Fe32Mn3A18Cr反铁磁精密电阻合金表面提拉制备Al2O3耐腐蚀防护涂层。采用X射线衍射分析涂层相结构,扫描电镜观察涂层表面形貌。在Fe32Mn3A18Cr合金表面形成连续、光滑的Al2O3涂层,具有（110）择优取向的γ-Al2O3结构。采用动电位阳极极化法测定涂层的电化学腐蚀性能表明,与原始合金相比较,在1mol／LNa2SO4溶液中,Al2O3涂层的自腐蚀电位提高了571 mV,自腐蚀电流密度降低了1个数量级以上,维钝电流密度降低了近1个数量级;在1％NaCl溶液中,自腐蚀电位与原始合金相当,自腐蚀电流密度降低了2个数量级,腐蚀电位高达2000mV（SCE）时仍未发生孔蚀击穿。而且,Al2O3防护涂层的耐均匀腐蚀和耐孔蚀性能均优于1Cr18Ni9Ti奥氏体钢。     

铁电-磁性复合薄膜的溶胶-凝胶法制备

用溶胶-凝胶法制备了Pb(Zr0.5Ti0.5)O3-Fe3O4复合薄膜。XRD研究表明,Pb(Zr0.5Ti0.5)O3呈完全(001)取向的,而Fe3O4颗粒则呈完全随机取向。在9V的测试电压下,薄膜的剩余极化Pr值为1.5μC/cm2;在1.5T的外磁场作用下,薄膜的剩余磁化强度和饱和磁化强度分别为0.67emu/cm3和3.5emu/cm3。铁电材料Pb(Zr0.5Ti0.5)O3与磁性纳米Fe3O4粒子的复合获得了室温共存的铁电性和磁性。     

溶胶-凝胶法纳米Al2O3涂层在钢材上的应用研究

利用溶胶-凝胶法制备了Al2O3溶胶,并在不锈钢、高碳钢、低碳钢等几种钢基材上进行涂敷,然后将其在1100℃高温下热处理腐蚀,通过表面结构的表征比较其抗氧化腐蚀性,并对有关问题进行了分析讨论。实验表明Al2O3溶胶涂层对钢板具有良好的保护作用,可有效防止钢板在高温下的氧化腐蚀。     

ZnO薄膜的溶胶-凝胶法制备及其光学性质研究

采用溶胶—凝胶法分别在透明玻璃和Si衬底上制备出了ZnO薄膜。分别采用X射线衍射仪(XRD)、能量分散谱仪(EDS)、紫外可见分光光度计和荧光光谱仪对所制样品进行测试,研究了样品的结构特性、成分和光学特性。X射线衍射结果表明,所制备的ZnO薄膜为六角纤锌矿结构;ZnO薄膜的EDS能谱图表明薄膜包含O元素和Zn元素;透射光谱表明ZnO薄膜质量高,在可见光范围内具有较高的透射率,平均透射率在85%以上;吸收光谱表明在带隙处存在吸收边;从PL光谱观察到了显著的紫外发射峰。     

Fe32Mn3Al8Cr反铁磁精密电阻合金Al_2O_3防护涂层的研究

用溶胶-凝胶法在Fe32Mn3A18Cr反铁磁精密电阻合金表面提拉制备Al2O3耐腐蚀防护涂层。采用X射线衍射分析涂层相结构,扫描电镜观察涂层表面形貌。在Fe32Mn3A18Cr合金表面形成连续、光滑的Al2O3涂层,具有（110）择优取向的γ-Al2O3结构。采用动电位阳极极化法测定涂层的电化学腐蚀性能表明,与原始合金相比较,在1mol／LNa2SO4溶液中,Al2O3涂层的自腐蚀电位提高了571 mV,自腐蚀电流密度降低了1个数量级以上,维钝电流密度降低了近1个数量级;在1％NaCl溶液中,自腐蚀电位与原始合金相当,自腐蚀电流密度降低了2个数量级,腐蚀电位高达2000mV（SCE）时仍未发生孔蚀击穿。而且,Al2O3防护涂层的耐均匀腐蚀和耐孔蚀性能均优于1Cr18Ni9Ti奥氏体钢。     

基于正交法的磁性Fe3O4纳米颗粒制备工艺选择

采用化学共沉淀法以FeCl3·6H2O,FeCl2·4H2O为原料,氨水为沉淀剂,进行了9组正交试验,探索制备Fe3O4纳米颗粒磁性能的影响因素,利用振动样品磁强计（VSM）和透射电镜（TEM）对磁粉进行表征,利用正交表极差分析找出了最佳制备工艺条件：即A2B1C3D2,去离子水用量为200 mL（Fe3＋为0.1 mol/L）;表面活性剂用量为1 mL;氨水30 mL;[Fe3＋]/[Fe2＋]=1.75时Fe3O4颗粒饱和磁化强度为62.70 emu/g.     

氧化铝粉体制备技术的进展与应用

综 近几年十年来国内外氧化铝粉体的历史与现状，各种常用制备技术的优缺点，氧化铝粉体的主要性能指标及其应用领域和前景，指出了今后有关高纯超细氧化铝粉体制备技术研究，开发和应用的方法。     

溶胶凝胶法制备ZAO薄膜

采用Sol-Gel法在普通载玻片上制备出C轴择优取向性、可导电的A l3 离子掺杂的ZnO透明导电薄膜.利用SEM、XRD等分析手段对薄膜进行了表征.研究结果表明:所制备的薄膜为六方纤锌矿型结构表面平整、致密.通过标准四探针法测定了A l3 离子掺杂的ZnO电阻率,证实了薄膜的导电性.实验发现,当离子掺杂浓度为1.5%,前处理温度为300℃,退火温度为600℃,薄膜的质量最好.     

Research on Reduction of Fe_2O_3 by Biomass Sawdust

The research on biomass reduction of Fe_2O_3 was carried out by using sawdust as reductant. The direct reducing agents in the biomass magnetization process were determined by comparing various biomass pyrolysis products with the reduction degree(divalent iron content in total iron), reduction temperature range and valence change of Fe_2O_3 in the reduction process. The microstructure variation of Fe_2O_3 at different stages was also analyzed by scanning electron microscopy(SEM). Nonisothermal thermogravimetric analysis(TGA) was applied to explore the thermal reduction process. The results show that the direct reducing substances in the biomass reaction with Fe_2O_3 are H_2 and bio-oil, and the reduction process can be divided into two steps: biomass pyrolyzing to release H_2 and bio-oil, and reductive volatiles reacting with Fe_2O_3. The two steps are relatively independent.The kinetic of the reduction reaction follows a first-order reaction kinetic model, with 88.99 k J/mol activation energy and 9.55 × 108min~(-1) frequency factor.     

Bi对YBa2Cu3O7—x结构和超导电性的影响

本文以电阻测定和 X 射线衍射分析,研究了 Bi 对 YBa_2Cu_3O_(7-x)结构和超导电性的影响.结果表明:在 YBa_2Cu_3O_(7-x)中加入 Bi,使体系中产生非超导相并降低其超导电性随着 Bi 含量的增加,在液氮温区其导电性由超导体向绝缘体转变.Bi 的加入只改变体系的组成相及其相对含量,并不改变超导相的正交性.加 Bi 的 YBacuO 的导电性对烧结温度很敏感,随着烧结温度的升高,超导电性迅速下降.     

水及水蒸气对YBa_2Cu_3O_(7-x)相结构及超导电性的影响

以热重分析(TGA)、X 射线衍射及电阻-温度关系测定等方法,研究了水及水蒸气于285-1223K 间对 YBa_2Cu_3O_(7-x)超导材料的超导电性退化、水解及热重变化等过程的影响.YBa_2Cu_3O_(7-x)试样在水及水蒸气冷凝于试样表面的水膜的作用下,将逐渐水解为 BaCO_3、CuO 及 Y_2O_3等产物.当试样或水蒸气的温度高于373K 时,水蒸气对YBa_2Cu_3O_(7-x)的晶体结构与超导电性无明显影响.在20%H_2O+80%O_2的气体介质中,YBa_2Cu_3O_(7-x)于373-1223K 问的 TGA 曲线与在常压大气中相似,其放-吸氧及相变过程是完全可逆的.自1223K 降温至373K,YBa_2Cu_3O_(7-x)恢复原来结构与性能.     

Al2O3陶瓷／Cu界面晶体位向关系对断裂性能的影响

以单晶α－Ａｌ２Ｏ３陶瓷和单晶Ｃｕ为母材,采用真空扩散焊接获得具有两种不同的界面晶体位向关系的Ｃｕ／Ａｌ２Ｏ３扩散焊接头以及带Ｎｂ膜中间层的Ｃｕ／Ｎｂ／Ａｌ２Ｏ３扩散焊接头,研究了面晶体位向关系对接头断裂能量的影响。     

固体超强酸SO4^2-/TiO2-Fe2O3的制备及其光催化性能

采用共沉淀-浸渍法制备了SO42-/TiO2-Fe2O3固体超强酸催化剂,通过样品光催化降解酸性蓝染料,考察了制备条件对染料脱色率的影响.结果表明,当固体酸中nTi和nFe的配比为1∶1,陈化pH为9~10,硫酸浸渍液浓度为0.5 mol/L,在500℃下焙烧4 h时制得的催化剂具有最高的催化活性.SO42-/TiO2-Fe2O3固体超强酸再生后催化活性基本不变,可重复使用.     

Al_2O_3/TiO_2的制备及光催化降解吡啶

以钛酸四丁酯为原料,Al2O3为载体,用溶胶-凝胶法制备负载型TiO2,在UV-TiO2体系中对吡啶(PD)进行光催化降解,并研究了将TiO2负载在不同铝源所制备的Al2O3后光催化剂的差异,结果表明:负载型TiO2光催化剂加入量为10mg/40mL,吡啶的光催化降解反应符合一级动力学方程;吡啶中氮转化成氨氮.将TiO2负载在Al2O3上后利用率提高了6倍左右.     

超声波均匀沉淀法制备Y2O3∶Eu3＋纳米晶及其荧光性能

在超声波作用下,使用均匀沉淀法制备了纳米Y2O3:Eu3+荧光粉,考察反应物配比、溶液pH值、反应时间、煅烧温度等制备条件对产物品粒尺寸及产率的影响.利用X射线粉末衍射(XRD)、等离子体原子发射光谱(ICP-AES)、透射电镜(TEM)和荧光光谱等测试手段表征产物,结果表明,该法制得的纳米Y2O3:Eu3+荧光粉颗粒为球形,粒度分布均匀,平均粒径约为30 nm.与微米晶相比,该纳米晶的激发光谱发生明显红移,电荷迁移态最大值(CTS)红移12 nm,发射光谱中发射主峰蓝移8 nm.