船用EH36高强钢无缝药芯焊丝焊接接头组织和冲击韧性研究

本文以SRSF501无缝药芯焊丝在船用EH36高强钢中的焊接应用为目的,研究了国产无缝药芯焊丝SRSF501在船用EH36高强钢焊接中的组织和冲击韧性。通过试验表明：SRSF501焊接EH36钢接头各区域的冲击性能均满足船级社要求;多层多道焊时,焊缝组织由粗大的柱状组织和细小的等轴晶组织组成,底层焊缝和末道焊缝柱状晶区域较大;盖面层两侧接头热影响区存在粗晶区,其它位置接头的热影响区不存在粗晶区;焊接接头中熔合线外2mm处,晶粒最细,冲击韧性最好。     

高弯拉强度水泥混凝土早期干缩变形性能研究

主要研究了水泥用量、胶凝材料类型、引气量、砂率等因素对混凝土干缩变形的影响。混凝土试件尺寸采用100 mm×100 mm×515mm,试验在控温控湿箱内进行,通过控温控湿箱的自动调节功能,设定目标温度和湿度过程,湿度按要求自动调节,利用千分表观察试件干湿变形值。湿度变化过程如下:从当前湿度用30 min升到相对湿度99%,恒定180 min,读取初值;用30 min降低湿度到10%,恒定180 min,读取终值;再用30 min升高湿度到99%,恒定180 min,读取初值,如此进行3个循环。试验结果表明:随水泥用量的增加,混凝土早期干缩变形增大;单掺硅灰的混凝土早期干湿变形大,单掺粉煤灰和混掺硅灰与粉煤灰的混凝土差别不大;3 d龄期的混凝土含气量越大,干湿变形也越大;28 d龄期以后,在含气量小于6.8%的情况下,干湿变形随含气量的增加而减小,而当含气量达到10%,干湿变形又呈现增大的趋势。     

耐碱玻璃纤维混凝土的抗弯冲击性能研究

耐碱玻璃纤维在混凝土中分散性良好,显著改善了混凝土的抗弯冲击性能。由梁弯曲冲击试验发现:当玻璃纤维掺量为1.6~2.7 kg/m3时,纤维掺量2.7 kg/m3(G 3)的初裂冲击次数比掺量2.0 kg/m3(G 2)和1.6 kg/m3(G 1)时分别提高1.97倍和2.81倍,比素混凝土提高10.97倍;G 2的初裂冲击次数比G 1提高28%,比素混凝土提高3.03倍。G 3的破坏冲击次数比G 2提高1.95倍,比G 1提高2.78倍,比素混凝土提高11.01倍;G 2的破坏冲击次数比G 1提高28%,比素混凝土提高3.08倍;G 1的破坏冲击次数比素混凝土提高2.18倍。纤维质量掺量由2.0 kg/m3提高到2.7 kg/m3时,对改善混凝土抗弯冲击性能效果十分显著。玻璃纤维显著改善了混凝土的抗弯冲击性能,可以用于机场道面、桥面等工程。     

路用高弯拉强度混凝土配制与施工技术要点

主要论述了高弯拉强度混凝土对水泥、集料、掺合料及外加剂等原材料的技术要求;提出路用高弯拉强度混凝土配合比设计原则与方法,并给出推荐的配合比范围;论述了高弯拉强度混凝土拌和、运输、摊铺、切缝和养护等施工过程中的技术控制要点。     

基于悬索桥修正成桥线形的索夹弯曲应力分析

为较精确地分析悬索桥成桥线形下索夹对主缆弯曲次内力的影响,基于成桥状态下的分段悬链线理论,考虑索夹的套箍作用修正成桥线形,使其更接近于实际线形.修正后的成桥线形近似为各段悬链线与短直线段交替连续的混合线形.以三汉矶大桥为例,利用有限元法计算出索夹端面处主缆的主拉应力及索夹相对转角,代入WYATT公式,计算出主缆在各个索...     

厚钢板CTOD试验中试样数量问题研究

针对试样数量的选择的问题,按照CTOD韧性试验规范BS7448,对多批不同试样进行试验,并分析和对比试验结果.发现由于离散性的存在,按NS-EN 10225-2009与《材料与焊接规范》要求的传统取样数量并不能准确地判断材料的韧性.参考DNV-OS-C401关于焊接接头CTOD特征值的选择方法,讨论3种试样选取的方法.最后考虑多方面的因素,建议每次制备6个试验试样.     

FWD在旧水泥混凝土路面弯拉弹性模量检测中的应用研究

结合莞深高速公路K0+000～K41+000段改扩建工程勘测设计的实际需要,按我国现行的相关技术规范要求,采用FWD的先进检测手段,对该路段水泥混凝土路面面板的动态弯沉及弯沉盆进行现场测定,在参考国内外研究成果的基础上,建立了弯拉弹性模量反算的数学模型,为旧路大修工程设计提供了路面性能评价依据和设计参数.     

The effect of plastic constraint on the initiation of ductile tears in shipbuilding structural steels

In this paper, the effect of plastic constraint on the initiation of ductile tears in four different shipbuilding structural steels has been experimentally studied by measuring the J-integral and crack opening displacement COD at initiation in three-point bend specimens with deep and shallow notches. Experimental results of seven groups of different strength alloy steels show that both Si and Ji values of ductile tear from the shallow crack specimens which have less constraint flow field are significantly higher than those of deeply notched specimens. Slip-line-field analysis shows that, for shallow crack, the hydrostatic stress is lower than that from standard deeply cracked bend specimen, which develops a high level of crack tip constraint, provides a lower bound estimate of toughness, and will ensure an unduly conservative approach when applied to structural defects, especially if initiation values of COD and J-integral are used.     

A review of the effect of a/W ratio on fracture toughness (I) —experimental investigation in EPFM

1INTRODUCTION Crackopeningdisplacement(COD)andtheJ in tegralastwoimportantfracture characterizingparame tersinelastic plasticfracturemechanics,arealready welldevelopedandusedinindustrialapplications.However,deeplycrackedstandardlaboratory specimenwhichhasahighlevelofconstraintmaynot alwaysberepresentativeofthosefoundinstructural components.Structuralcomponentsoftenexhibitcom parativelyshallowandsurface breaking,andtheplas ticflowassociatedwiththemreachesthesurfaceofthe component.Inthisca…     

运用二阶摄动方法预测焊接点疲劳微弯裂纹的路径发展

利用二阶摄动方法分析研究了轻微弯曲疲劳裂纹尖端应力强度因子的变化幅度,进一步得到了在循环载荷下直线裂纹微弯延伸尖端应力强度因子变化幅值的近似表达式.以匹配渐进扩张的形式考虑了远区域边界条件的效果,研究了裂尖附近的渐进应力场.利用Irwin公式计算出了由于裂纹发展而引起的应变能释放率变化幅值.预测了在具有非均匀断裂韧度的物质中裂纹的延伸.考虑了循环载荷、残余应力,以及由于焊接而引起的物质衰变等因素,利用了二阶摄动方法预测了沿着焊接点传播的弹脆性裂纹路径.