低温下复合材料层合板的层间应力分析

以低温推进剂的纤维增强树脂基复合材料燃料罐为对象,研究在低温环境下复合材料/结构的力学性能。基于细观力学模型,分别建立了用于复合材料贮箱的2种典型复合材料E-Glass/Epoxy和Graphite/Epoxy低温环境下的本构关系。采用有限元法,通过对低温环境下典型铺层的层合板自由边界附近层间应力的分析,讨论了低温对E-Glass/Epoxy和Graphite/Epoxy这2种典型复合材料层合板自由边界附近层间应力分布的影响。结果表明:温度的变化对层合板层间应力分布的影响较明显,且温度越低层合板的最大层间应力值越大。研究成果将对低温推进剂的纤维增强树脂基复合材料燃料罐设计提供一定的参考价值。     

采用中频逆变电阻焊和闪光对焊焊接圆环链的对比研究

文中采用中频逆变电阻焊技术和闪光对焊技术分别焊接大直径高等级圆环链.对比研究了两种焊接工艺过程特点,分析了接头微观组织形貌、断口形貌和接头性能之间的相互关系.结果表明:中频逆变电阻焊技术的编链和焊接工艺过程比闪光对焊生产自动化程度高、生产效率高、生产环境好、焊后无需清除毛刺.在各自最优工艺参数条件下,中频逆变电阻焊对焊圆环链所得接头性能比闪光对焊所得性能好,产品合格率高.     

An improved ductile fracture criterion for fine-blanking process

In order to accurately simulate the fine-blanking process, a suitable ductile fracture is significant.So an evaluation strategy based on experimental and corresponding simulation results of tensile, compression, torsion and fine-blanking test is designed to evaluate five typical ductile fracture criteria, which are widely-used in metal forming process.The stress triaxiality and ductile damage of each test specimen are analyzed.The results show that none of these five criteria is sufficient for all tests.Furthermore, an improved fracture criterion based on Rice and Tracey model, taking the influence of both volume change and shape change of voids into account, is proposed.The characterization of this model for fine-blanking process is easily done by the tensile test and the prediction result shows good.     

半刚性基层沥青路面温缩型反射裂缝的扩展机理分析

通过对半刚性基层在温度应力作用下裂缝扩展机理的分析,以线弹性断裂力学理论和有限单元方法为基础、利用ANSYS计算软件,研究了产生反射裂缝的力学机理,分析了各参数对含裂纹路面结构的应力场以及裂纹尖端应力强度因子的影响。结果表明,得出裂纹尖端的应力集中是导致裂缝向上扩展的根本原因,降低基层材料的弹性模量能抑制或延缓基层裂缝的扩展;当裂缝已经反射到面层后,降低面层材料的弹性模量也可以起到抑制或延缓基层裂缝的扩展;同时,外界环境和路面结构对裂缝的扩展亦有较大的影响,应根据当地的气候条件合理地设计沥青面层和基层的厚度,以保证路面结构具有预期设计的抗裂性。为防止或减少反射性裂缝有重要的参考价值。     

柔性纤维混凝土(砂浆)断裂能试验研究

混凝土材料的断裂能是一个最为重要的混凝土非线性断裂力学参数,其大小标志着材料裂纹扩展的难易程度,对分析混凝土结构的性能有重要指导意义。通过几种柔性纤维混凝土（砂浆）试件的断裂能对比试验,研究不同纤维对混凝土（砂浆）试件断裂性能的影响,得出了一些有益的结论,为桥梁设计、施工和加固提供参考。     

基于强度折减法的海底边坡三维稳定性分析*

为了分析波浪荷载作用下海底边坡的稳定性,通过Visual C#语言平台开发数值接口程序,实现了地质三维建模程序Gocad和有限元分析程序Abaqus的数据转换,即有限元程序在海底复杂的地貌和地形条件下三维建模。同时开发了Abaqus力学场数据处理程序,可以实现Abaqus在强度折减法下的边坡稳定性分析。通过分析波浪作用下舟山朱家尖岛海域海底边坡稳定性,评判该边坡的稳定性。计算结果表明,波浪荷载对海底边坡稳定性会产生一定的影响,朱家尖岛附近海域海底边坡有滑坡的风险。     

Non-fatal spine injuries resulting from motorcycle crashes

This study aims to determine spinal injury patterns and identify crash factors commonly associated with serious spinal injury as a result of motorcycle crashes. Data was retrospectively collected from motorcyclists sustaining spinal injuries from road crashes treated at Kuala Lumpur Hospital, Malaysia, over the 5-year period from 2005 to 2009. Each patient's injuries were analyzed by reviewing his or her medical records for radiographic imaging and computed tomography scans.A total of 151 patients were included in this study, of which, males accounted for over 87%. The first lower lumbar (L1) was the most commonly injured vertebral level, followed by the adjacent thoracic vertebra (T12). Fracture to the vertebral body without dislocation was found to be the most frequently observed spinal injury pattern. Injury severities for a majority of patients (65%) were measured at Maximum Abbreviated Injury Scale (MAIS) of 2. Serious spinal injury was associated with thorax or upper-extremity injury.Prevalence of lumbar spinal injury in the study reflects a predominantly low-speed crash among the motorcyclist in the region. Motorcyclists are at greater odd to sustain severe spinal injury when directly striking an object compare to striking the ground during the crash event.     

断层破碎带巷道基于钢管混凝土支架的复合支护技术研究及应用

为解决阳城煤矿-650南翼轨道大巷断层破碎带支护中出现的围岩变形大和变形持续时间长等问题,采用室内实验、理论计算和支护实践相结合的方法,对-650南翼轨道大巷围岩地质进行测试研究,揭示巷道原有支护变形破坏机制,提出断层破碎带巷道承压环强化支护设计方法,并由此设计基于钢管混凝土支架的复合支护设计方案。实验及理论分析得出： 钢管混凝土支架支护反力为0.92 MPa,基于钢管混凝土支架的复合支护体总体承载力达到1.37 MPa,超过预估围岩压力。支护实践表明： 基于194 mm×8 mm浅底拱圆形钢管混凝土支架复合支护方案能够有效控制巷道变形,抑制底鼓,保证了-650南翼轨道大巷的长期稳定。     

基于光频域反射技术的破碎带盾构隧道管片监测研究

为探究盾构施工过程中不同地质条件与注浆作用对盾构隧道管片变形的影响规律,依托地质条件复杂的珠江三角洲某盾构隧道工程,采用在空间分辨率及传感精度方面具有显著优势的光频域反射（OFDR）分布式光纤传感技术,进行不同空间位置与不同地质条件下隧道管片的监测研究。其中,监测环选取位于破碎带外的1 529环、1 538环及破碎带内的1 551环,传感光纤沿隧道管片钢筋笼纵筋布设。研究表明： 1) 注浆对隧道管片的变形影响十分显著,同步注浆后管片发生的变形是二次注浆后管片变形的3倍。2) 不同地质条件下管片变形差异性明显,破碎带内管片相对于破碎带外管片的变形较大且不稳定; 当隧道管片进入到完整的岩层内部,管片变形相对稳定。3) 破碎带内的管片变形是破碎带外的管片变形的2.6倍。     

EH36船用钢焊接角变形有限元分析

采用有限元分析方法,根据实际焊接工艺过程,对船舶常用低温高强钢EH36中厚板的二道焊缝焊接温度场及焊接角变形进行了分析.中厚板焊接常为二道的埋弧焊接,在有限元分析中采用生死单元技术进行处理.有限元分析结果显示焊接温度场关于热源中心对称,同一厚度截面方向的节点处的焊接变形相同,而在横向由于焊缝在厚度方向收缩的不均匀性,处于焊缝间隙大的截面的节点焊接变形要大于处于小间隙截面的节点.实验结果证明了有限元分析的准确性.