土工格栅加筋粉煤灰堤坝的室内模拟试验研究

通过室内小比例尺模型试验,模拟了双向土工格栅在粉煤灰堤坝中相同边坡坡比下,未加筋与加1层、2层筋等不同结构形式在坡顶荷载作用下坡顶沉降和边坡的变形规律,研究了土工格栅加筋参数对堤坝边坡结构性能的影响。试验结果表明,加筋能大幅提高堤坝的稳定性和承载能力,对工程实践具有一定的指导意义。     

碱激发粉煤灰水泥胶凝体系的水化机理分析

通过在粉煤灰掺量比例为50%的粉煤灰-水泥胶凝体系中加入Na_2SO_4和碱石灰复合激发进行粉煤灰火山灰活性激发试验,研究粉煤灰-水泥胶凝体系的早期强度,并采用衍射分析和扫描电镜分析硬化浆体的微观结构.研究结果表明:Na_2SO_4和碱石灰复掺具有明显的活性作用.水泥石早期强度显著提高;水泥石中形成了较多的CSH和AFt,未发现AFm生成,说明加入Na_2SO_4和碱石灰共同激发可有效破坏粉煤灰的玻璃微珠外壳及硅铝网络结构,可增强粉煤灰的潜在活性.     

高性能纤维素纤维及其混杂纤维混凝土的弯曲疲劳特性

系统研究了高性能纤维素纤维、钢纤维、纤维素纤维及钢纤维混杂纤维混凝土的弯曲疲劳特性,探讨了龄期对纤维素纤维增强粉煤灰混凝土疲劳性能的影响。试验表明:纤维素纤维混凝土疲劳强度比素混凝土提高6.8%;纤维素纤维与钢纤维联合使用后,构件的弯曲疲劳性有了较为显著的改善,钢纤维掺量64 kg/m3与纤维素纤维掺量1.3 kg/m3混掺时,混杂纤维混凝土比单掺钢纤维64 kg/m3的混凝土疲劳强度提高15.4%。即混杂纤维将会充分发挥各种纤维的优势,对改善疲劳性能的作用比单掺钢纤维和纤维素纤维都显著。纤维素纤维增强粉煤灰混凝土70 d时疲劳强度比34 d提高11%。     

土工格栅与粉煤灰在路堤中的耦合作用试验研究

根据粉煤灰和土工格栅的特性,利用室内模型试验对粉煤灰和土工格栅路堤的工程性质进行研究,对于指导设计和施工具有一定的实际意义.     

膨胀土粉煤灰改性与石灰改性对比试验研究

开展了典型中膨胀土、粉煤灰改性土与石灰改性土的基本物理特性、击实特性、强度特性比较试验。试验结果表明:1)相比于未改性土,粉煤灰改性土和石灰改性土自由膨胀率、塑性指数、胶粒含量都显著降低;2)随着粉煤灰掺入比的增大,在重型击实标准下,改性土最优含水量呈增大趋势,最大干密度呈下降趋势;3)两种改性土CBR峰值都显著提高,当掺入比合适时,CBR膨胀量显著降低,改性后水稳定性较好;4)两种改性土都可同时满足规范对压实度和CBR的要求。最后探讨了与石灰相比粉煤灰改性方案的适用性与可行性。     

水泥(粉煤灰)稳定煤气化多孔炉渣抗冻性能研究

为研究煤气化多孔炉渣路面基层材料的抗冻性能,采用炉渣100％ 替代天然集料制备了水泥稳定炉渣和水泥粉煤灰稳定炉渣,分析不同冻融循环次数下,水泥(粉煤灰)稳定炉渣的质量损失和冻融残留抗压强度比(BDR)变化,并与水泥稳定碎石进行对比.结果表明,水泥(粉煤灰)稳定炉渣经5次冻融循环后BDR可达94.1％ 以上,均高于水泥稳...     

Chloride diffusion models for Type I and fly ash cement concrete exposed to field and laboratory conditions

The exposure temperature significantly affects the diffusion of chloride ions in concrete, and, as such, it must be taken into consideration in the development of service-life prediction models for structures exposed to chloride-bearing environments. Most of the earlier studies have used cement paste to assess the effect of exposure temperature on chloride diffusion. In the reported study, chloride diffusion in Type I and fly ash (20% fly ash) cement concrete was evaluated under field and laboratory conditions. The laboratory concrete specimens were exposed to chloride solution maintained at four temperatures (22, 35, 50 and 60 °C) for 365 days. Beam specimens were exposed in the tidal zone of a marine exposure site, along the Arabian Gulf coast, for up to 10 years to study the chloride diffusion in the field specimens. The coefficient of chloride diffusion (D_a) in the concrete specimens exposed to 22 or 35 ᵒC in the laboratory was less than that in the concrete specimens exposed to 50 and 60 ᵒC. The D_a for Type I cement concrete specimens increased by 3.6 times as the temperature was increased from 22 to 60 ᵒC while this increase was 2.3 times for the fly ash cement concrete specimens for a similar increase in the temperature. The D_a decreased with the period of exposure in the field specimens. The values of activation energy that can be used for predicting the chloride diffusion for exposure temperature within the range of 22–60 °C were developed based on the laboratory data. In addition, mathematical models were developed relating the coefficient of chloride diffusion in the field and laboratory concrete specimens. The developed models can be utilized to ascertain chloride diffusion in field specimens, utilizing the laboratory values, and hence calculate the useful service-life of structures.     

机制砂高性能混凝土在高速公路工程中的应用研究

针对机制砂混凝土应用中出现的级配不良,结合重庆沿江高速工程实际,通过分析不同配合比下机制砂混凝土的工作性能、力学性能、耐久性能,提出改善措施。结果表明：机制砂混凝土的坍落度损失较大,粉煤灰对其有明显改善作用;机制砂级配不良时,抗压强度不能满足使用要求,需掺配河砂调整级配。提出机制砂质量不稳定等是机制砂在高性能混凝土中应用受到制约的主要原因,并提出推广机制砂在高性能混凝土中应用的建议。     

石灰改良路基土的力学特性试验研究

以上海某新建道路工程浅层路基土为研究对象,对不同掺灰量的石灰改良土进行击实试验、界限含水率和三轴剪切试验,研究掺灰量对其最大干密度、最优含水率和液塑限的影响规律,以及掺灰量和围压对石灰改良土抗剪强度指标有效粘聚力c′和有效内摩擦角φ′的影响。试验研究结果表明:随着掺灰量的增加,石灰改良土最大干密度减小,最优含水率增加;掺灰量对石灰土的界限含水率指标影响较大,尤其是对液限的影响最为明显,对于塑限,9 %左右的掺灰量对其影响最大;当掺灰量大于某个值时,石灰改良土强度随着围压和掺灰量的增加而增加,随着掺灰量的增     

二灰钢渣混合料路用性能试验

为了研究二灰钢渣混合料的路用性能,进行了3种配比的二灰钢渣混合料抗冻性能、干缩性能、抗冲刷性能试验,并与二灰碎石类集料对比分析.结果表明:二灰钢渣的抗冻性能优于二灰碎石,而其干缩系数明显小于同配比二灰碎石;配比为5:15:80的二灰钢渣抗冻性能、抗干缩性能、抗冲刷性能均最优.