Fe-Mn-Al与Fe-Mn奥氏体合金的高温氧化性能与组织结构

运用循环氧化与增重-时间法、扫描电镜(SEM)及X射线衍射分析(XRD)等技术研究了Fe-30Mn-5Al与Fe-25Mn合金在700℃～800℃空气中氧化的性状 在700℃,Fe-30Mn-5Al合金由于Al的优先氧化在其表面形成了Al2O3薄膜而提高其抗氧化性,氧化动力学规律由Fe-25Mn的直线性(Q0.9631=0 9661×t)规律转变为抛物线规律(Q1.967=0.0869×t) 800℃时,由于氧化物的生长速率指数上升,氧化层显著增厚,循环氧化剥落严重,氧化动力学遵循亚平方抛物线规律(Q1.559=2.49×t) 初步阐明了合金元素Mn、Al及氧化温度对Fe-Mn基合金抗高温氧化性能的影响     

生产玻璃模具用耐热铸铁的研究

本文从玻璃模具的服役条件与失效形式出发,分析了对材质的要求,研制了一种新的用于制做玻璃模具的耐热铸铁材料.通过对材质的抗氧化、抗生长、热疲劳、热扩散以及导热系数的实验与测定,结果表明:蠕虫状 Gr-Mo 合金铸铁是用于制做玻璃模具的比较理想的材料,用这种材料和中频炉、冲天炉熔化生产的模具经现场使用,其寿命分别达到45万次和40万次以上,超过了目前国内生产的各种铸铁玻璃模具的使用寿命.     

Si—Mo蠕虫状合金耐热铸铁的研究

本文从玻璃模具的服役条件与失效形式出发,分析了其对材质的要求,研制了一种Si-Mo 蠕虫状合金耐热铸铁.在对其机械性能、抗氧化、抗生长性能,热疲劳性能、导热性能及热扩散性能进行测试的基础上,系统分析了合金元素及石墨形态对各项性能的影响.实验结果表明:Si-Mo 蠕虫状合金耐热铸铁具有良好的综合使用性能,是一种制做玻璃模具的理想材料.     

微弧氧化陶瓷表面无钯活化化学镀铜的研究

用氢氟酸活化方法取代传统的钯胶活化法,在镁合金微弧氧化陶瓷膜表面经化学镀铜制备了陶瓷／铜协合膜层。结果表明,铜层连续均匀地覆盖微弧氧化陶瓷层表面,渗入并填充陶瓷层内部呈网状分布的孔隙,实现了铜层与陶瓷层在呈网络状分布的孔隙处产生机械咬合、钉扎或锁扣。以价健理论分析了材料表面析氢电催化活性过程,探讨了微弧氧化陶瓷层表面氢氟酸活化机理。     

Reaction characteristics of the diesel oxidation catalyst of particulate matters from the diffusion flame of a oiler burner

The objective of this experimental study is to investigate the characteristics of the size distribution and the number concentration of PM (particulate matters) emitted from the diffusion flame of a boiler burner, which has the same type of combustion as a diesel engine. This study is performed to investigate the emission characteristics of nanoparticles generated from diffusion combustion in diesel fuel, and it considered fuel factors and the reaction characteristics of the nanoparticles on the DOC (Diesel oxidation catalyst). The factors examined in this experiment included the sulfur content in the fuel, the blend of the diesel fuel containing biodiesel and bio-ethanol, and the concentration of engine oil (0.1% and 1.0%) blended with diesel fuel. The particle size distribution of the nanoparticles exhausted from the boiler burner was measured by an SMPS (scanning mobility particle sizer). The number concentration of PM that were smaller than 70 nm in diameter greatly increased in the rear of the DOC when fuel containing 250 ppm of sulfur was used. The experiment also suggested that the particle number concentration in both the front and rear of the DOC was lower when ULSD (ultra low sulfur diesel) fuel blended with biodiesel and bio-ethanol, which are oxygenated fuels, was used than when only ULSD fuel was used. The higher the content of engine oil in the fuel, the higher the particle number concentration was in the front and rear of the catalyst. When the first dilution air temperature is increased from 30°C to 180°C, the nanoparticle number concentration dramatically dropped in the rear of the catalyst when fuel containing 250 ppm of sulfur was used, while the particle size distribution remained almost the same when the fuel with engine oil was used.     

苏州市横扇生活污水处理厂提标改造工程设计

苏州市吴江横扇污水处理厂提标改造工程规模0.5万m3/d,改造内容包括新建二级提升泵房、反硝化深床滤池、消毒池、污泥浓缩池、除臭生物滤池、鼓风机房及配电间等设施。同时对现状AAO氧化沟进行改造,由转碟曝气改为底部鼓风曝气。工程建设完成后,出水水质优于地表准Ⅳ类标准,有效地改善了周边的水体环境。     

微粒氧化催化器与催化型燃油添加剂联合降低重型柴油车微粒排放的试验研究

在低、中、高3种转速及不同扭矩的工况下对重型柴油车进行了PM排放试验,对比了微粒氧化催化器(POC)+柴油机氧化催化剂(DOC)和POC+燃媒催化型燃油添加剂两种PM净化方案。试验研究表明,添加剂最佳添加质量分数为90×10-6,添加剂可替代DOC与POC联合净化PM,并得到较为理想的净化效果。     

硅钨酸光催化降解甲基橙溶液研究

以硅钨酸为光催化剂,研究了其对模拟染料废水甲基橙的光催化脱色卫生解影响,结果表明,酸度、催化剂投加量、溶液初始浓度是影响催化降解效果的重要因素,最佳催化条件为,10mg/L的甲基橙溶液在紫外灯辐照下,硅钨酸浓度0.4g/L,溶液酸度pH=1,其对甲橙溶液光催化降解效果比磷钨酸差。     

纯铜的表面弥散硬化及其性能

用渗铝－内氧化技术对纯铜进行了表面弥散硬化处理。研究了渗层的铝浓度分布，硬化层的为微特性及有关性能。结果表明，渗层的铝浓度接近于渗占的铝粉含量，渗层深度可达１００μｍ，内氧化后，能在铜的渗铝怪形成Ａｌ２Ｏ３弥散硬化层。Ａｌ２Ｏ３含量影响了铜的表面硬度，电阻率及磨损能力。     

高浓度有机废水超临界水氧化技术应用

结合洋口临港工业园高浓度有机废水无害化处理示范项目实例,简述超临界水氧化处理原理、工艺设计和实施流程。通过开展中试试验,利用超临界水处理技术处理某厂高浓度废水,观察超临界技术对废水处理效果,分析探讨该技术在工程应用中可能存在的问题及优化方向。