PD3余热淬火钢轨接触焊焊后热处理研究

淬火钢轨接触焊后存在接头晶粒粗化,塑性、韧性大幅度下降,硬度不均匀等现象,使用中钢轨焊接接头的脆性增大,产生接头低塌并导致马鞍形磨耗和波浪磨耗。为解决上述问题,PD3余热淬火钢轨接触焊后必须对焊接接头进行焊后热处理。焊后热处理采用中频感应加热,加热温度为845℃～920℃,然后喷风冷却接头全断面,喷风压力0 25MPa～0 30MPa,喷风冷却时间120s。结果表明,接头经热处理后的硬度、韧塑性能接近或超过原淬火轨水平,落锤、静弯、实物疲劳性能有较大的提高,满足了无缝线路钢轨的使用要求。     

Modelling and handling dynamics of a wind-driven vehicle

This paper presents a study on the dynamic modelling of a land-yacht, i.e. a ground vehicle that is propelled by wind energy through the use of a vertical airfoil. First, a non-linear dynamic model of the land-yacht motion is derived using a compact matrix notation. Then, an introduction to the study of the performance and handling characteristics is presented. It is considered the vehicle response to input commands, i.e. steering to follow the desired course and adjusting the sail angle according to environmental conditions, that is, wind intensity and direction. The model demonstrates the performance in terms of maximum longitudinal speed and the effects on handling behaviour of the major vehicle design and operational parameters, including location of the centre of gravity and centre of effort, and forward speed, and it leads to conclusions of practical significance concerning directional control and stability.     

轻轨车辆用耐候钢冲压性能及工艺参数试验研究

本文论述了耐候钢耐腐蚀及高强度的特点,给出了其经试验得到的有关冲压性能和冲压工艺参数,为拟定工艺和设计模具提供了依据.     

五河口斜拉桥索塔高性能混凝土试验研究

结合五河口斜拉桥索塔工程研究了两种粉煤灰和粗骨料对高性能混凝土的力学性能影响,通过对粗骨料品种、粉煤灰品种及其掺量进行优化,得到了满足工作性和强度要求的索塔C50高性能混凝土配合比,并对其物理力学性能、耐久性能进行了检验。     

DC and AC transport properties on La0.8Sr0.2MnO3

Magnetoresistive sensor can be widely used in modem transportation field, such as the vehicle positioning and navigation system, vehicle detection system, and intelligent transportation system. In order to improve the efficiency of magnetoresistive sensor, we synthesized Lao.sSro.2MnO3 polycrystalline bulks at different sintering temperatures and investigated their DC and AC transport properties in this work. As a result, all samples showed insulator-metal （I-M） phase transition, and the transition temperature （TI-M） shifted to higher temperature with the increase of sintering temperature. The TI-M measured at different AC frequencies was smaller than that measured at DC condition, which implied that the I-M phase transition was suppressed at AC frequencies. The resistivity mea- sured at high AC frequencies was larger than that measured at low AC frequencies, which could be attributed to the change of the magnetic penetration depth （6）. However, the room-temperature AC-magnetoresistance （MR） at low frequencies was much larger than that at high frequencies and room-temperature DC-MR. These findings demon- strate that reducing the AC frequency is an effective way for enhancing the room-temperature MR, which can be used to promote the efficiency of magnetoresistive sensor.     

Ⅰ型和Ⅱ型静动态统一本构关系及用于分析回跳现象

在工型静动态统一本构关系的基础上,建立了Ⅱ型静动态统一本构关系,分别用Ⅰ型和Ⅱ型本构关系分析了有回跳特性的材料的力学行为.Ⅰ型本构关系以应变和温度为作用量,Ⅱ型本构关系以Ⅱ型应变和温度为作用量,Ⅱ型应变是应力和应变的线性组合.有回跳特性的材料在受到单调增加的轴向应变作用时,会经历弹性阶段、时间无关不可逆变化阶段、伴随有应力跌落的时间相关不可逆变化阶段以及最后的时间无关不可逆变化阶段.对应于每一个阶段,工型本构关系都有相应的判据和计算公式.有回跳现象的单轴压缩应力-应变曲线,按照时间顺序可分为,应变单调增加的弹性阶段、应变单调增加的时间无关不可逆变化阶段、应变减小的时间无关不可逆阶段（回跳阶段）以及之后的应变再单调增加的时间无关不可逆阶段.在每一个阶段,Ⅱ型本构关系都有对应的判别准则和计算公式,Ⅱ型本构关系覆盖了有回跳特性的材料遇到的各种可能工况.     

海底混响统计特性的仿真和试验验证

基于混响统计特性的瑞利分布模型和K分布模型,推导并给出了基于物理散射的单基地海底混响数学模型,并分别采用CW和LFM信号对数学模型进行了仿真,对仿真数据进行了瑞利分布和K分布拟合检验,对湖试试验数据处理后进行了瑞利分布和K分布拟合检验,验证了海底混响数学模型和仿真方法的正确性.结果表明：K分布模型能更精确的描述海底混响的统计特性.     

掺入泵送剂全尾砂膏体流变特性研究

以新疆某铜矿全尾砂为主要原料,研究了泵送剂掺量、质量分数和废石添加量对膏体流变特性的影响.试验结果表明：泵送剂掺量控制在2%左右便可达到最佳流变效果;屈服应力和塑性粘度与膏体质量分数间分别成指数和二次函数关系;随着废石添加量增多,屈服应力呈单调递减趋势,塑性粘度则无明显变化规律.以恒减速速率模拟浆体在管道中输送过程,发现膏体在流入采空区后仍能保持初始流变性能,说明泵送剂适用于该矿山膏体充填.     

改性沥青及混合料流变学性能研究

利用扫描电子显微镜（SEM）、动态剪切流变试验（DSR）、小梁弯曲蠕变试验及三轴压缩蠕变试验,分别从微观和宏观角度对比研究了胶粉改性沥青（CR）和SBS改性沥青及其混合料的微观结构、高温及低温对其流变性能的影响。SEM试验结果表明,橡胶粉及SBS改性剂都能与沥青达到良好共融,但在沥青混合料中胶粉改性沥青与石料界面的粘结性要优于SBS改性沥青;DSR试验结果表明,CR具有更好的温度稳定性、低温抗裂能力和高温抗变形能力;小梁弯曲蠕变试验在-15、0、15、30,45℃5种温度下对比研究了配合比相同的2种沥青混合料,得到不同温度下的弯曲蠕变速率对比曲线,试验结果表明,CR混合料比SBS改性沥青混合料具有更好的高、低温性能;此外,还进行了45℃下2种沥青混合料的三轴压缩蠕变试验,证明CR沥青混合料具有更好的抗高温变形特性。     

钢筋混凝土结构地震破坏机理的材料分析

在工程结构的抗灾研究中,首要关注的是材料受灾后的性能变化,即灾害对材料物理力学性能的影响,亦即材料在灾害作用下的损伤。文章从分析钢筋混凝土结构受地震作用后的损害机理入手,结合材料内部性能的改变,探讨了结构损害的根本原因,并提出合理有效的改善措施,以减少地震多发区的灾害损失。