低温球磨制备块体纳米Al晶体材料的组织与性能

采用低温球磨结合真空热压烧结技术制备了块体纳米Al晶体材料,并加入硬质Al2O3颗粒来进一步提高该材料的强度和硬度．利用X射线衍射,透射电镜对材料的微观组织进行了分析和观察,并对所制备块体纳米材料的密度、显微硬度和拉伸性能进行了测定．研究结果表明：当球磨时间从8h增加到14h时,纳米Al粉末颗粒的晶粒尺寸从55nm减小到43nm,微观应变从0．0272％增至0．0759％．经致密化处理后,该材料的晶粒尺寸从115nm减小到71nm．经热挤压后的块体纳米Al及Al—Al2O3晶体材料的相对密度都达99．4％以上,其最高显微维氏硬度分别为1．02和1．22GPa,比粗晶Al的显微维氏硬度分别提高了3和3．6倍．块体纳米Al的最高屈服强度和抗拉强度分别为165和243MPa,比粗晶1050纯Al的屈服强度和抗拉强度分别提高了7．5和3．2倍．当平均晶粒尺寸小于223nm时,得到块体纳米Al材料的屈服强度与晶粒尺寸之间的关系为σ=71．8＋1．8D^-1/2．     

S355J2W耐候钢焊接接头显微组织与力学性能

通过拉伸、疲劳和金相检验试验,对S355J2W耐候钢、空冷状态焊接接头和退火状态焊接接头进行了显微组织和力学性能的研究.结果表明：两种状态焊接接头的力学性能都达到了要求,S355J2W耐候钢退火状态焊接接头的强度低于空冷状态焊接接头的强度;退火状态焊接接头的塑性好于空冷状态焊接接头的塑性;退火状态焊接接头的疲劳寿命低于空冷状态焊接接头的疲劳寿命;退火状态焊接接头与空冷状态焊接接头相比,每个区域的晶粒都有明显的细化和均匀化,空冷状态的焊接接头显微组织的晶界比较清晰.     

高铝600MPa级冷轧双相钢的试验研究与分析

对一种高铝600MPa级冷轧双相钢进行了试验研究和分析.结果表明:该双相钢具有优良的力学性能;其连续冷却相变温度为Ac3=930℃,Ac1=770℃;退火组织为典型的铁素体+岛状马氏体双相组织,马氏体均匀分布在铁素体周围;马氏体岛附近的铁素体基体中存在高密度自由位错.     

热处理对锰硼白口铁机械性能与显微组织的影响

研究了淬火、回火温度、冷却介质对锰硼白口铁机械性能及显微组织的影响。结果表明:淬火硬度随淬火温度提高出现峰值,峰值位置随淬火冷却速度增加向温度低的方向移动;回火硬度随回火温度升高在250℃出现峰值,回火温度高于480℃后硬度显著降低;残留奥氏体随回火温度升高而减少,430℃回火残留奥氏体基本消失,转变产物为贝氏体;淬火回火提高强韧性。     

双相化处理工艺对冷拔双相钢丝组织和性能的影响

研究了08Mn2Si钢不同工艺处理后双相组织的形态及冷拔中组织与性能的变化,结果得到:950℃预淬火后再经临界区加热淬火时可以得到细小均匀的纤维状双相组枳,这种组织在冷拔中转变为很细的平行于拔丝方向的纤维状组织,且具有最好的强度和韧性。     

Effect of Gr Content and Hot Extrusion on Tensile Properties of （Nano-SiCp~-Gr）/Cu Composites Fabricated by Powder Metallurgy

Novel hybrid Cu matrix composites reinforced by graphite (Gr) particle with volume fraction of 5%?C15% and nano-SiC particle (nano-SiCp) with volume fraction of 3% have been prepared by powder metallurgy. The results show that Gr and nano-SiCp distribute uniformly in the Cu matrix. With increasing the volume fraction of Gr, the tensile strength of the composites decreases from 114 to 51MPa and the elastic modulus decreases from 75 to 60GPa. Compared with the sintered composites, the tensile properties including elastic modulus, tensile strength, yield strength and tensile elongation of the hot-extruded (nano-SiCp+Gr)/Cu composites are improved greatly due to higher relative density of the composites and more uniform distribution of Gr and nano-SiCp, in addition to finer grain size of the matrix as a result of dynamic recovery and recrystallization which occur during hot extrusion process.     

Microstructure and property of friction stir welding joint of 7075Al and AZ31BMg

Microstructure and forming quality of friction stir welding joints of 7075Al and AZ31BMg with different welding parameters were analyzed. The results show that, good welded joint is obtained when the rotating frequency is 13 r/s and the welding speed is 30 mm/min. An irregular area is formed in the welding center. Meanwhile, the river pattern and eddy-like distribution are found in the weld nugget zone. Besides, brittle intermetallic compounds Al₁₂Mg₁₇ and Al₃Mg₂ are found in the welded joint. They cause the increase of microhardness of welded joint. The maximum tension stress of welded joint is 112MPa.     

船用EH36高强钢无缝药芯焊丝焊接接头组织和冲击韧性研究

本文以SRSF501无缝药芯焊丝在船用EH36高强钢中的焊接应用为目的,研究了国产无缝药芯焊丝SRSF501在船用EH36高强钢焊接中的组织和冲击韧性。通过试验表明：SRSF501焊接EH36钢接头各区域的冲击性能均满足船级社要求;多层多道焊时,焊缝组织由粗大的柱状组织和细小的等轴晶组织组成,底层焊缝和末道焊缝柱状晶区域较大;盖面层两侧接头热影响区存在粗晶区,其它位置接头的热影响区不存在粗晶区;焊接接头中熔合线外2mm处,晶粒最细,冲击韧性最好。     

氩弧钎焊工艺对镀锌钢板表面锌层影响研究

针对电弧钎焊连接镀锌钢板时的锌层破坏行为进行了系统的研究,使用氩气作为保护气体,分别对当电流为直流和交流,燃弧时间从1s至5s时的镀锌钢板表面宏观形貌和微观形貌进行了分析。结果表明当采用直流电弧加热镀锌钢板时表面Zn层除蒸发外,还有熔化并形成FeZn合金表层熔膜,但基体Q235钢没发生熔化。但因交流电弧"阴极锌层气化-剥离作用"使表面锌层严重破坏,并影响钎料的润湿铺展,因此交流电弧不能连接镀锌钢板。     

NaOH含量对AZ91D镁合金微弧氧化膜层微观结构和耐蚀性的影响

在由15 g/L Na2SiO3、12 g/L NaAlO2、3 g/L Na2B4O7、5 mL/L C3H8O3、5 g/L C6H5Na3O7及1~4 g/L NaOH组成的硅铝复合电解液中,利用微弧氧化技术在AZ91D镁合金基体上制备了一系列陶瓷膜层.利用扫描电镜、膜层测厚仪分别研究了陶瓷膜层的微观结构及厚度;采用全浸泡实验和交流阻抗实验测试了膜层在3.5%NaCl溶液中的耐蚀性能.结果表明：随着NaOH含量的增加,微弧氧化过程中的起弧电压和终止电压均呈线性下降;膜层的耐蚀性随着NaOH含量的增加先提高后降低,膜厚的变化趋势与其耐蚀性的变化趋势基本一致;NaOH含量的变化主要影响膜层内部致密层的耐蚀性能;当NaOH含量为2 g/L时,膜层最厚,膜层较致密,因而具有较好的耐蚀性能.