Improvement the electrochemical performance of Li1.2Ni0.2Mn0.6O2 electrode with AlF3 added

Layered solid solution material Li_1.2Ni_0.2Mn_0.6O₂ is synthesized and the AlF₃ is added to improve the electrochemical performance. X-ray diffraction (XRD) results show that the Li_1.2Ni_0.2Mn_0.6O₂ samples exhibit layered characteristics. The AlF₃ additive is detected by transmission electron microscope (TEM) technology. The electrochemical tests show that Li_1.2Ni_0.2Mn_0.6O₂ electrode with AlF₃ added delivers better discharge capacity (240mA· h/g), first coulomb efficiency 79.2%, cyclic performance (capacity retention ratio of 100.6% after 50 cycles), and rate capacity (68mA · h/g at 10 capacity (C)) than the pristine sample. Electrochemical impedance spectroscopy (EIS) results show that the charge transfer resistance of Li_1.2Ni_0.2Mn_0.6O₂ electrode with AlF₃ added increases slower than that of pristine Li_1.2Ni_0.2Mn_0.6O₂ after cycling, which is responsible for better cyclic and rate performance.