非标准养生温度下二灰稳定碎石路用性能试验研究

通过大量的室内试验，研究了二灰稳定碎石在10 ℃的低温环境下养生的无侧限抗压强度、劈裂强度及增长趋势。试验研究结果表明:与标准养生温度相比，在10 ℃养生环境下，二灰稳定碎石的抗压强度和劈裂强度等物理力学指标大为降低且增长缓慢，7天龄期抗压强度仅为0.43～0.67 MPa，是标准养生温度下的1/3左右，达不到相关技术规范要求，路用性能受到严重影响。因此，建议在低温季节进行二灰稳定碎石基层施工时，要采取一些有效措施来保障其强度的形成。

Test Study on Pavement Performance of Lime-flyash Stabilized Aggregates under Non-standard Curing Temperature

In this paper,a large number of laboratory tests were done to study the unconfined compressive strength,splitting strength and growth trends of lime-flyash stabilized aggregates under the curing condition of the low temperature at 10 ℃.The test result shows that under the curing condition of 10 ℃,the physical and mechanical indexes of lime-flyash stabilized aggregates,such as compressive strength,splitting strength,when compared with the standard curing temperature,become much lower and grow slowly;7 days compressive strength is 0.43~0.67 MPa,which is just only about 1/3 of that under the standard curing temperature and can’t meet the relevant technical specifications,thus pavement performance was affected severely.Therefore,when lime-flyash stabilized aggregates base was constructed in lower-temperature seasons,the author suggests that some effective measures must be taken to protect formation of the strength.