| 钢结构厚板对接焊缝低温冲击韧性试验研究 |
| |
| 引用本文： | 王元清,胡宗文,石永久,周晖,陈宏.钢结构厚板对接焊缝低温冲击韧性试验研究[J].铁道科学与工程学报,2010,7(5). |
| |
| 作者姓名： | 王元清 胡宗文 石永久 周晖 陈宏 |
| |
| 作者单位： | 清华大学,土木工程安全与耐久教育部重点实验室,北京,100084;清华大学,建筑设计研究院,北京,100084 |
| |
| 基金项目： | 国家自然科学基金资助项目(50778102) |
| |
| 摘 要： | 目前,国内建筑物在不断地超高层化以及超大型化,使得钢结构厚板的应用越来越广泛。厚度增大导致焊缝焊接热影响增大,同时焊缝的缺陷敏感性也相对更加显著,这些因素使得钢厚板焊缝韧性性能变差,特别是在低温环境中更加明显。因此,有必要研究钢厚板对接焊缝的低温冲击韧性。对150 mm厚钢板对接焊缝进行了低温下的冲击韧性试验研究,结果显示焊缝区和热影响区的冲击韧性均随温度降低而降低,而且热影响区的冲击韧性沿板厚度方向随表面到中心的位置变化而降低,这和母材的规律一致,但数值相对母材有所降低。同时,利用Boltzm ann函数对试验结果进行拟合分析,得到其韧脆转变温度及变化规律。试验结果表明:钢结构特厚板对接焊缝有较明显的低温脆性特征,要引起足够重视。
|
| 关 键 词： | 钢结构厚板 对接焊缝 热影响区 低温 冲击试验 韧脆转变温度 |
Experimental study on the impact toughness of thick plate butt weld of steel structure at low temperature |
| |
| WANG Yuan-qing
,
HU Zong-wen
,
SHI Yong-jiu
,
ZHOU Hui
,
CHEN Hong.Experimental study on the impact toughness of thick plate butt weld of steel structure at low temperature[J].Journal of Railway Science and Engineering,2010,7(5). |
| |
| Authors: | WANG Yuan-qing HU Zong-wen SHI Yong-jiu ZHOU Hui CHEN Hong |
| |
| Institution: | WANG Yuan-qing1,HU Zong-wen1,SHI Yong-jiu1,ZHOU Hui1,CHEN Hong2(1.Key laboratory of Civil Engineering Safety , Durability of China Education Ministry,Tsinghua University,Beijing 100084,China,2.Architectural Design , Research Institute,China) |
| |
| Abstract: | Within buildings becoming higher and larger continuously,steel thick plate is used more and more widely.Thickness increase leads to the increase of heat-affect,and the sensitivity of weld defects is also relatively more significant,which causes the weld toughness performance of steel thick plate to get worse,especially in the low-temperature environment.Therefore,it is very necessary to study the impact toughness of weld of steel thick plate.This paper carried out an experimental study on the impact toughne... |
| |
| Keywords: | thick plate of steel structure butt weld heat-affect zone low temperature impact toughness test ductile-brittle transition temperature |