The paper studied the effect of Ni-Fe-C filler materials on the η phase formation during TIG welding of WC-30Co and 45 steel, η phase‘s morphology and forming condition were discussed using I3EI method. The properties of the weld joints were also measured using microhardness measurement and four-point bending measurement. The results show that the weld joints of WC-30Co/45 steel can be obtained by TIG welding using different Ni-Fe-C materials as filler materials, and η phase formed in the joints is M6C, M12C type carbides. The poor carbon content of the W-Co-C system resulted from the C diffusion and the high ingredient Fe are the two vital factors inducing to η phase formation. It can be restricted by the addition of C element into Ni-Fe material. When carbon content is 0. 01% in filler material, bend strength σbb of weld joint is 908 MPa. However, when carbon content increases to 0.41% in filler material, bend strength σbb is 1 260 MPa.     

汽车用铝合金激光+TIG复合焊接工艺研究

对汽车用3A21铝合金的激光复合焊接工艺(激光 TIG)进行了研究,探讨了工艺参数对焊缝成型的影响规律及激光与电弧的复合作用。试验结果表明,激光焊复合工艺可以显著提高焊缝熔深和焊接速度,从而实现采用小功率激光焊机实现铝合金激光焊接的目的。在较宽的工艺参数范围内,YAG激光复合焊接铝合金具有焊缝成型美观等优点,且可大大提高生产率。     

哈氏合金导电辊失效机理研究

哈氏合金以其优良的抗腐蚀性能广泛应用于强腐蚀介质的环境中,但钨极氩弧焊焊接的哈氏合金导电辊提前失效。研究针对哈氏合金导电辊在使用过程中产生开裂导致失效的原因展开分析,从宏观和微观金相、断口形貌、EDAX分析及电化学腐蚀来确定提前失效的机制,为下一步开展制造哈氏合金导电辊工艺提供理论依据和技术指导。     

Research on electron beam welding of in situ TiB<Subscript>2p</Subscript>/ZL101 composite

Electron beam welding of in situ TiB_2p reinforced aluminum composites was studied. The results show that no obvious pores or cracks is presented in the weld seam. The grains in the weld seam are remarkably refined and TiB₂ particles distribute much more homogeneously than that in base metal. The hardness values of fusion zone and heat affected zone (HAZ) are both increased in comparison with that of base metal. There are no interface reactions between TiB₂ particle and Al matrix. This results supply the evidence that the novel TiB_2p reinforced aluminum composites can be well joined with the electron beam welding.     

Study on the Formation of η Phase During TIG Welding

The paper studied the effect of Ni-Fe-C filler materials on the η phase formation during TIG welding of WC-30Co and 45 steel. ηphase's morphology and forming condition were discussed using BEI method. The properties of the weld joints were also measured using microhardness measurement and four-point bending measurement. The results show that the weld joints of WC-30Co/45 steel can be obtained by TIG welding using different Ni-Fe-C materials as filler materials, and ηphase formed in the joints is M6C, M12C type carbides. The poor carbon content of the W-Co-C system resulted from the C diffusion and the high ingredient Fe are the two vital factors inducing to ηphase formation. It can be restricted by the addition of C element into Ni-Fe material. When carbon content is 0.01 % in filler material, bend strength σbb of weld joint is 908 MPa. However, when carbon content increases to 0. 41% in filler material, bend strength σbb is 1 260 MPa.