冷铺沥青材料的特性与配制技术

用冷铺沥青混合料修补路面坑洞,具有方便、快捷等优点.为保证其疏松性和压实性,在配制方法上,如所用沥青的粘度、沥青的用量、添加剂以及集料级配等,与热拌沥青混合料都有很大区别.实践表明,所研制开发的冷铺材料使用性能良好,而成本却比同类进口材料大大降低.     

船舶焊接CO2气体保护单面焊气孔成因探讨

ＣＯ２气体保护半自动单面焊用于船舶焊接，提高了焊接质量，减轻了焊工的劳动强度，半缩短了造船周期。但是单面焊打底层焊缝中出现的沿焊缝柱状晶结晶方向的柱状气孔，严重地影响着船舶焊接质量。     

氧化铁皮对CO2半自动单面焊气孔倾向的影响

本文就坡口上的氧化铁皮对ＣＯ_２半自动陶质衬垫单面焊气孔倾向的影响进行了试验研究,利用Ｘ射线检测、ＯＭ、ＳＥＭ、ＥＤＸ和ＸＲＤ等方法对焊道进行了宏观及徽观分析。结果表明,氧化铁皮主要由Ｆｅ_３Ｏ_４、Ｆｅ_２Ｏ_３和ＦｅＯ组成,并参与反应生成ＣＯ气体;打底层焊缝中形成大量夹杂物易于气泡的形核;陶质衬垫的保温作用使打底层焊道上部先于底部结晶,气泡不易逸出而形成气孔。本文还探讨了防止气孔产生的措施。     

晋北地区黄土湿陷系数与其物理力学性质的相关性分析

通过对晋北地区大量的黄土室内湿陷性试验数据进行分析,研究黄土湿陷系数与天然孔隙比、天然密度、天然含水量、压缩模量、塑性指数和液性指数6种常规物性参数之间的相关性,结果显示:黄土湿陷系数与天然孔隙比之间呈正相关关系;与天然密度、天然含水量、压缩模量、塑性指数和液性指数呈负相关关系;探讨不同湿陷强度黄土的天然孔隙比、天然密度、天然含水量及液性指数的分布规律,结果显示:该地区湿陷性黄土的天然孔隙比大于0.6,天然密度小于1.9 g/cm~3,天然含水量小于22%,液性指数小于0.25。     

焊前预处理对AlSi10MgMn真空压铸件与铝型材MIG焊接气孔的影响

AlSi10MgMn真空压铸铝合金在MIG焊接存在气孔,其连接方式的选择一定程度上受限,通过对Al?Si10MgMn真空压铸铝合金和型材件进行焊前预处理(氧化皮打磨、酒精清洗、预热处理)后进行MIG焊接,分析了该方案对于焊接气孔的改善效果,结果发现焊前预处理对AlSi10MgMn真空压铸铝合金和型材件MIG焊接气孔改善效果明显,焊缝接头剖面平均气孔率由1.14%降低为0.73%,同时发现焊缝接头剖面中心区域显微硬度值最高,接头强度为180 MPa,接头效率为75%,焊前预处理对显微硬度和接头强度基本无影响。     

沥青混合料空隙率影响因素分析

以抗滑表层AK-16级配混合料,采用不同的击实功成型试件,分别进行马歇尔试验、浸水残留稳定度试验、劈裂抗拉强度试验、冻融劈裂试验及动稳定度等试验,分析沥青混合料空隙率的影响因素。     

排水性沥青路面在香炉礁立交桥扩建工程中的应用

排水性沥青路面具有迅速排除路面表面水、降低行车噪音、抗滑能力强等特点.阐述了排水性沥青混合料在实际工程中材料要求、试验结果以及实际应用的效果.     

Sediment physical properties of the DYNAS study area

Physical properties of the deposits in the DYNAS study area, the Mecklenburg Bay, were investigated using sediment echosounders and laboratory analysis were carried out on undisturbed short sediment cores. Wet bulk densities of about 1.2 g/cm³ for mud and up to 1.9 g/cm³ for silty sand were found in surface sediments of the Mecklenburg Bay. Sediment density–depth functions were approximated by logarithmic regression functions at different depth intervals. Sediment consolidation was studied by both (i) consolidation tests of sediment samples and (ii) from the void ratio–overburden pressure relation in natural sediments. Low shear strength values of 9–71 Pa were measured at the mud surface. Downcore, a depth gradient of about 14.5 Pa/cm was calculated. Sediments with high silt and sand contents are characterized by shear strength values of up to 3000 Pa. Published formulas derived from erosion studies were used to calculate the critical shear stress using wet bulk density and shear strength. The obtained results demonstrate clearly, that there is still a wide gap in knowledge about the relationships between erosion parameters and sediment physical properties.     

AC-13(改进型)沥青混合料劈裂试验研究

文章结合柳州绕城高速公路AC-13(改进型)沥青混合料矿料级配,利用SGC旋转压实机成型沥青混合料试件并进行劈裂试验,对AC-13(改进型)沥青混合料的间接抗拉强度进行评价,得出沥青混合料的空隙率、油石比、老化这些指标的变化与沥青混合料的力学特性间的密切关系。     

沥青路面压实度和空隙率的变异性分析

沥青混合料路面的压实度与空隙率是路面施工的重要质量检测指标,是沥青路面使用寿命最基本的保证.压实度与空隙率由于受原材料、混合料配合比设计、施工工艺和施工温度等因素的影响,会造成矿料骨架结构的变化,影响混合料的结构和强度;压实度与空隙率的变异性会影响到路面的强度、耐久性和防水性等,当路面发生脱粒、坑槽、渗水等病害时,追寻病害根源,分析压实度与空隙率的变异性是必要的.