悬浮式双镀膜冷却辊连续镀膜设备的研制

高真空悬浮式双镀膜冷却辊连续镀膜设备的研制生产彻底解决了传统的单镀膜冷却辊镀膜对薄膜材料造成的局部起褶暴筋和产生白条纹(镀空线)的问题,显著提高了镀膜速度和产品质量,降低了废口率,为新一代真空连续镀膜设备开辟了新的应用领域和市场前景.本文主要介绍了高真空悬浮式双镀膜冷却辊连续镀膜设备的原理、组成、性能及工作过程,并对相关问题进行了讨论分析.     

二氧化钛膜光催化降解脱色甲基橙

用溶胶-凝胶法制备了不同载体、不同层数的锐钛矿纳米TiO2薄膜.利用TiO2薄膜作催化剂,光催化降解甲基橙溶液.研究了载体、光源、镀膜层数、pH值、初始浓度等对光催化降解脱色率的影响,从中获得了最佳镀膜及最佳光催化条件.结果表明:以太阳光为光源,以铝合金为载体,在500℃条件下镀3层膜,且在pH<8.00时光催化脱色效果最好;且该反应为表观一级反应,该光催化反应的极限速率常数为0.40 mg/(L.min),吸附平衡常数为2.65 L/mg;表面反应而非吸附是这个光催化反应的速度决定步骤,即该反应符合Langmuir-Hinshewood(L-H)机理.     

镍／聚四氟乙烯复合电镀新工艺的研究

利用电沉积方法制取了镍/聚四氟乙烯复合膜，研究了电流密度、温度、表面活性剂、预镀等因素对复合镀膜的影响，从而得取了最佳工艺条件，结果表明镀膜质量良好，耐磨性大大提高。     

二氧化钛膜光催化降解脱色甲基橙

用溶胶-凝胶法制备了不同载体、不同层数的锐钛矿纳米TiO2薄膜.利用TiO2薄膜作催化剂,光催化降解甲基橙溶液.研究了载体、光源、镀膜层数、Ph值、初始浓度等对光催化降解脱色率的影响,从中获得了最佳镀膜及最佳光催化条件.结果表明:以太阳光为光源,以铝合金为载体,在500℃条件下镀3层膜,且在Ph＜8.00时光催化脱色效果最好;且该反应为表观一级反应,该光催化反应的极限速率常数为 0.40 mg/(L·min),吸附平衡常数为2.65 L/mg;表面反应而非吸附是这个光催化反应的速度决定步骤,即该反应符合Langmuir-Hinshewood (L-H)机理.     

铸造Al-Si合金表面气相沉积TiN薄膜的耐磨性能

采用多弧离子镀技术,对铸造Al-Si合金表面气相沉积TiN薄膜的耐磨性能进行了研究。结果表明,镀有TiN薄膜的铸造Al-Si合金具有比未镀膜铸造Al-Si合金更优异的耐磨性。在相同的磨损条件下,未镀膜试样表面由于发生磨粒磨损,在磨损过程中出现严重的微观切削现象;TiN涂层表面以粘着磨损为主,其磨痕存在剥落,并且随着磨损时间的延长,磨损机制由粘着磨损转为磨粒磨损,未镀膜试样的磨痕宽度几乎是TiN磨痕的2倍。     

“膜”术大师

不镀膜、不喷漆,可穿隐形甲,能披七彩衣,车身贴膜让爱车始终光亮如新、时刻变化。从汽车诞生以来,人类追求汽车养护的脚步从未停止。为了让爱车始终光亮如新,我们想了很多办法,提高漆面亮度、减少漆面损伤的打蜡诞生了。为了追求更长久、有效的保护效果,有了封釉、镀膜技术的出现。但随着科技的发达,我们对汽车车身养护的要求也越来越多,要更简便、更实用、更时尚,于是车身贴膜也就顺势而生了。     

频闪动态干涉法测量离面位移的研究

频闪视觉测量和频闪干涉测量代表了目前先进的微机电系统动态测试技术,尤其在非接触无损测量技术有重要意义.通过微机电三维静动态测试系统,综合运用等厚干涉原理和基片曲率法,实时测量,计算出镀膜样品在升温和退火过程中应力的变化.结果表明,该方法适合测量微机电器件的离面位移.     

真空蒸发镀膜法制备TiO2薄膜及其催化活性

用真空蒸发镀膜法在铜、玻璃板、不锈钢板3种不同材料上负载了TiO2薄膜,并用扫描电镜(SEM)和能量色散谱(EDS)对薄膜进行表征与分析.以苯酚废水为对象进行了光催化降解试验,研究了3种不同基材TiO2薄膜的光催化活性.与商品TiO2粉末的悬浮态光催化试验对比,该方法制备的TiO2薄膜具有催化剂用量少,活性高,易回收的优点.不同基材的TiO2薄膜光催化活性有所不同,不锈钢板较好,玻璃板次之,铜板最差.     

人美靠衣车靓靠膜

车漆镜面镀膜技术,是世界最新一代的车漆保护技术.它最早出现在堪称汽车美容王国的日本岛,所用材料不含任何石油成分,不含研磨材料,而是由玻璃素原子、氟素高分子体、透明纤维分子采用特殊工艺精制而成,具有防护力强、光洁明亮、强度超高、清洗方便、无副作用、效果持久等优点.     

薄膜弹性模量测定的四点弯曲法

提出了一种新的薄膜弹性模量测定方法－四点弯曲法，首先，推导出镀膜之后的复合梁及镀膜之前的基材梁弯曲到同一挠度下的载荷比（F2／F1）与薄膜和基材的弹性模量之比（Ef/Es)的关系，然后分别利用基材梁试件及离子镀Ag-Cu/Ti双层膜复合梁试件在四点弯曲实验下的挠曲线，便可计算得到Ag-Cu/Ti双层膜的弹性模量，实验结果表明，此方法避免了纳米压力测弹性模量时的压痕尺寸效应，故该方法为一种测量薄膜弹性模量的简单、可靠的方法。     

镍—钼—磷／聚四氟乙烯复合电沉积工艺研究

在镍－钼－磷（Ni-Mo-P)合金电镀液中加入聚四氟乙烯（PTFE）制得了镍－钼－磷／聚四氟乙烯（Ni-Mo-P/PTFE)复合镀层。研究了镀液主要成份及工艺条件对复合镀层的影响，优选出一种较佳的工艺条件及复合镀液配方。由复合镀层性能测试结果发现，与Ni-Mo-P合金相比，由于PTFE的加入，提高了复合镀层的减摩性，但结合力与硬度略有下降。     

INFLUENCE OF SURFACE MORPHOLOGY ON THE MICROHARDNESS OF ELECTROLEESS NI-B DEPOSIT REVEALED BY AFM OBSERVATION

A crystalline and non-crystalline two-phase Ni-B coating was prepared by electroless deposition with potassium borohydride as reducing agent. When the deposit was heated from 10 C to 500 C, it took place three kinds of phase transformation and formed corresponding nickel borides. An Atomic Force Microscopy (AFM) was used to directly view the surface morphologies of the samples in various treated states. The AFM images indicate that nano-dimensional protrusions grow on the surface of the deposit grain during some heat treatment processes,and they are distinguished greatly from the small bulges existing in the as-plated deposit. Further studies show that the microhardness related to the surface topography of thecoating to some extent. Especially when a two-step heat treatment process was performed, the nano-dimensional protrusions on the grain surface grew upt to 40～100nm in diameter and 10～20 nm in height, and the deposit microhardness reached up to HV1500～ 1600 in the meantime.     

工艺因素对铸铁热浸渗铝的影响

通过表面制备方法、热浸温度和时间等工艺因素对铸铁热浸渗铝影响的试验和分析,获得了热浸温度和时间与浸渗层组织、铁的溶解深度及浸渗铝质量的关系,指出了适宜的表面制备方法。     

关于桥梁深长钻孔灌注桩施工若干问题研究

介绍福建省罗(源)长(乐)高速公路A8标段海积层和沉积层地层深长钻孔灌注桩施工方法,重点对钻进成孔工艺、特殊地层钻孔成桩技术、深孔灌注钢筋混凝土桩等作详细的论述。     

平原区低路堤高速公路排水系统研究

研究了下挖通道处的排水系统和小于淤积坡度路段路表排水系统。对于下挖通道排水系统,提出了渗井、防雨棚、蒸发池和泵站4种排水方案,并对这4种方案进行了对比和评价。在路肩以及中央分隔带的路缘带设置的纵向集水沟与路基边坡上的急流槽等组成了小于淤积坡度路段路表排水系统。结果表明:防雨棚适用范围广,蒸发池仅适用于干旱和半干旱地区,泵站可应用于立交或比较重要的通道;小于淤积坡度路段路表排水系统不会发生失稳破坏,经济效益好,不易淤积。     

陕西省眉县和华阴县农村已婚育龄妇女RTI/STD患病现状及影响因素分析

目的了解陕西省眉县和华阴县农村已婚育龄妇女生殖道感染及性传播疾病(RTI/STD)患病现状及影响因素。方法采用分层整群抽样方法抽取陕西省眉县和华阴县共4304例已婚育龄妇女进行RTI/STD的患病现状、相关知识和行为现况调查。结果RTI/STD总患病率为63.80%,慢性宫颈炎的患病率为60.84%,霉菌、滴虫、尖锐湿疣总患病率为8.20%。RTI/STD患病的影响因素有年龄、宗教信仰、家庭经济水平、丈夫外出打工时间、生育活产数、自然流产史、避孕方式、夏天洗澡地点、冬天洗澡周期、夫妻性生活周期。结论陕西省眉县和华阴县农村已婚育龄妇女RTI/STD患病率处于全国较高水平,家庭经济水平、个体婚育特征和卫生习惯是RTI/STD患病的主要影响因素。     

基于微球孔内团聚的多孔钛表面药物释放技术

通过含药物的微球在骨植入材料表面微孔内团聚方法解决现有骨植入材料表面药物释放技术缺乏通用性、无法控制释放速度的问题.用乳液法合成负载不同含量庆大霉素的壳聚糖微球粉末,并使其铺散于多孔钛层表面后进入孔内.经水润湿后,微球在孔内团聚并被固定于孔内.实验结果表明:水浴振荡试验7 d(100 r/min, 37 ℃)后, 80%~83%的微球仍位于多孔钛层内,微球-多孔钛复合物表现出初期(24 h)快速释放和后期( 24 h)缓慢释放;金黄色葡萄球菌培养48 h后,多孔钛与载庆大霉素微球的复合物产生了抑菌圈.      

三乙醇胺含量对化学浴法制备硫化铜薄膜的影响

为了研究三乙醇胺(TEA)在化学水域沉积法工艺中的作用,本文以氯化铜, 硫脲, 氨水和三乙醇胺为原料, 采用化学浴沉积法在玻璃基底表面成功制备了硫化铜薄膜. 研究了三乙醇胺不同含量对薄膜的厚度、结构,、形貌和光学性能的影响, 并分析了反应机理. 研究结果表明:三乙醇胺在反应中起到络合剂的作用,随着三乙醇胺含量的增加, 反应诱导时间延长到23 min; 沉积时间相同的情况下,组成薄膜的颗粒粒径变大且薄膜增厚240 nm, 同时透射率呈现出减小的趋势.      