EA4T车轴钢的超声冲击表面强化

利用超声冲击设备对EA4T车轴钢进行了表面强化处理.采利用金相显微镜和透射电镜表征了车轴钢表面结构的变化,并对超声冲击处理前后试样表面粗糙度和显微硬度进行了分析.结果表明:经超声冲击处理后,试样表面发生了剧烈的塑性变形,晶粒明显细化,显微硬度呈梯度化.随着超声冲击功率的增加,变形层厚度增加,粗糙度减小,表面硬度增大;与未经超声冲击处理的试样相比,在超声冲击功率180瓦作用下,表面粗糙度降低了6.5倍,试样的表面硬度提高了25%,变形层厚度大约为80μm.     

焊后退火工艺对S355J2W钢焊接接头力学性能的影响

通过显微硬度试验、室温冲击试验和冲击试样显微断口形貌分析,对空冷和退火两种处理的S355J2W钢焊接接头进行了性能研究．结果表明：适当的退火工艺可以降低焊接接头的硬度,消除其残余应力,使焊接接头的组织分布更加均匀,提高焊接接头各微区的冲击性能．     

Effects on Microstructure and Properties of Brass Treated by Laser Shock Processing

Laser shock processing （LSP） has been proposed as a new surface treatment for improving hardness, wear resistance and fatigue. In this paper, the effect of LSP on brass is investigated with experiment. Micro-hardness, roughness, microstructure, wear resistance and friction coefficient evolution are investigated for different parameters of LSP. The result shows that the roughness increases after LSP; no ablation is observed; the microstructure has no remarkable ehange; hardness and the wear resistance increase as the pulse density increases.     

闭孔泡沫铝与铝及铝合金覆板的冶金结合

利用直接冶金结合方法,研究了铝及铝合金覆板的厚度及复合温度与时间对闭孔泡沫铝夹心三明治与覆板结合层厚度的影响.利用金相显微镜观察了泡沫铝夹心与覆板结合界面的微观组织,并测量了结合界面的扩散层厚度和显微硬度.研究结果表明,铝熔体与纯铝和铝合金覆板复合温度越高,复合时间越长,他们之间的扩散层厚度越大;当纯铝板的预热温度为400~450℃,复合速度为53.9~74.4 mm/min时,泡沫铝夹芯与纯铝板形成良好冶金结合,复合界面的互扩散层厚度为39~44μm;当铝合金覆板的预热温度为240℃,复合速度为58.3 mm/min时,制备铝合金覆板泡沫铝三明治所需的铝合金板最小厚度应为7.9 mm.     

磨削方式对65Mn钢磨削淬硬层及其均匀性的影响

采用刚玉砂轮在卧轴矩台平面磨床上对65Mn钢进行了磨削淬硬,研究了磨削方式对65Mn钢磨削淬硬层组织、显微硬度、淬硬层深度及其均匀性的影响.结果表明:磨削方式对磨削淬硬层显微组织及其显微硬度无显著影响,淬硬层完全淬硬区均由细小均匀的针状马氏体、残余奥氏体和少量未溶碳化物组成,淬硬层高硬度值均在760～820HV之间;但随着磨削方式的改变,试件淬硬层深度及其均匀性相应改变.采用逆磨+顺磨或顺磨+逆磨+顺磨不仅可以增加磨削淬硬层深度,而且可以提高磨削淬硬层深度的均匀性.