低温球磨制备块体纳米Al晶体材料的组织与性能

采用低温球磨结合真空热压烧结技术制备了块体纳米Al晶体材料,并加入硬质Al2O3颗粒来进一步提高该材料的强度和硬度．利用X射线衍射,透射电镜对材料的微观组织进行了分析和观察,并对所制备块体纳米材料的密度、显微硬度和拉伸性能进行了测定．研究结果表明：当球磨时间从8h增加到14h时,纳米Al粉末颗粒的晶粒尺寸从55nm减小到43nm,微观应变从0．0272％增至0．0759％．经致密化处理后,该材料的晶粒尺寸从115nm减小到71nm．经热挤压后的块体纳米Al及Al—Al2O3晶体材料的相对密度都达99．4％以上,其最高显微维氏硬度分别为1．02和1．22GPa,比粗晶Al的显微维氏硬度分别提高了3和3．6倍．块体纳米Al的最高屈服强度和抗拉强度分别为165和243MPa,比粗晶1050纯Al的屈服强度和抗拉强度分别提高了7．5和3．2倍．当平均晶粒尺寸小于223nm时,得到块体纳米Al材料的屈服强度与晶粒尺寸之间的关系为σ=71．8＋1．8D^-1/2．     

深冷球磨及真空热压制备块体Al及Al-Al2O3纳米晶体材料

利用深冷球磨及真空热压技术制备块体Al及Al-Al2O3纳米晶体材料,采用X射线衍射测定晶粒尺寸,利用扫描电镜对材料的微观组织进行观察,并测定了所制备材料的显微硬度和抗拉性能.研究结果表明:经深冷球磨14 h后,Al粉末颗粒的平均晶粒尺寸由50 μm变化到43 nm.块体纳米Al晶体材料的显微硬度随烧结温度升高而下降,加入纳米Al2O3颗粒后显微硬度约为粗晶纯Al显微硬度的4倍;块体纳米Al晶体材料的抗拉强度极限σb为265 MPa,加入纳米Al2O3颗粒后的抗拉强度为322 MPa,比纳米纯Al晶体材料提高了22%.     

深冷球磨及真空热压制备块体Al及Al-Al_2O_3纳米晶体材料

利用深冷球磨及真空热压技术制备块体Al及Al-Al2O3纳米晶体材料,采用X射线衍射测定晶粒尺寸,利用扫描电镜对材料的微观组织进行观察,并测定了所制备材料的显微硬度和抗拉性能.研究结果表明:经深冷球磨14 h后,Al粉末颗粒的平均晶粒尺寸由50μm变化到43 nm.块体纳米Al晶体材料的显微硬度随烧结温度升高而下降,加入纳米Al2O3颗粒后显微硬度约为粗晶纯Al显微硬度的4倍;块体纳米Al晶体材料的抗拉强度极限σb为265 MPa,加入纳米Al2O3颗粒后的抗拉强度为322 MPa,比纳米纯Al晶体材料提高了22%.     

纳米金属Ni的塑性变形机制

为了深入探讨纳米金属的力学性能特别是塑性变形机制，对纳米金属Ni进行了不同程度的冷轧变形．通过x射线衍射分析和透射电镜观察对纳米金属Ni的微观结构和变形机制进行了研究，并对不同变形量下的晶格常数进行了计算．研究表明，随变形量增大，纳米晶体的晶粒尺寸逐渐增大，从最初的16．6nm增大到28．7nm，这种增长是由于部分方向（区域）晶粒长大的结果；变形量较小（小于30％）时，位错的活动与晶粒旋转是的变形主要方式，变形量较大（超过30％）时，晶界发射不全位错与孪晶的交互作用协调变形；纳米Ni的平均晶格常数为0．3533nm，略高于粗晶Ni的晶格常数．     

高能球磨对TiC0.5/Cu（Al）复合材料组织和性能的影响

以Ti2AlC和Cu粉作为原料,分别采用滚筒球磨和高能球磨对原料粉进行预混处理,在1 150℃下原位热压反应制备了TiC0.5/Cu（Al）复合材料.实验结果表明,Al从Ti2AlC溶出进入Cu中,Ti2AlC分解并转变成TiC0.5相,然而滚筒球磨制备的复合材料中生成少量AlCu2Ti相.通过对原料粉高能球磨处理,制备后的复合材料AlCu2Ti相消失,细小的TiC0.5颗粒均匀分布于基体中.两种不同方法制备的复合材料的弯曲强度和维氏硬度试验结果表明,高能球磨工艺能提高TiC0.5/Cu（Al）复合材料的弯曲强度,同时维氏硬度略有降低.其中,高能球磨处理后制备的27％ TiC0.5/Cu（Al）复合材料的弯曲强度达到981 MPa,维氏硬度为2.43 GPa.     

30Mn23Al4Cr5超低温无磁钢的冷加工强化

本文研究了冷加工对30Mn23Al4Cr5超低温无磁钢硬度、强度、塑性和冲击韧性的影响,试验结果表明,随着冷轧比的增加,硬度和屈服强度按抛物线规律增加,塑性和韧性按抛物线规律降低,而抗拉强度近似线性增加,冷轧引起的位错塞积和形变孪晶结构导致强度增加及塑性与韧性降低。     

溶胶-凝胶法制备软磁纳米材料Fe2O3

首次采用添加分散剂溶胶-凝胶法制备软磁纳米材料Fe2O3，采取添加分散剂和改变焙烧方法保证晶粒尺寸．实验结果表明：软磁纳米晶制备中添加分散剂尿素，然后在高温(600℃)焙烧前增加一个低温(400℃)退火阶段，两项措施能保证Fe2O3原始晶粒尺寸在30～40nm．试验操作简单、过程易于控制、产品质量稳定。     

Ti17合金电子束焊接接头组织和性能

通过室温拉伸试验、室温缺口拉伸试验、显微硬度试验以及金相分析对Ti17合金电子束焊接接头的显微组织和性能进行了研究.试验结果表明:用电子束焊接Ti17合金可获得性能良好的焊接接头,其接头的抗拉强度不低于母材,焊缝的缺口敏感系数均小于1.焊缝区和热影响区的硬度均高于母材,焊缝区组织与母材组织基本相同,都是α相上分布着沿晶界及晶内析出的细针状β相,焊缝区的晶粒度要比母材的晶粒度粗大.     

车辆车体耐候钢双相化热处理工艺及性能研究

研究了铁路机车车辆用两种热轧耐侯钢经热处理双相化后的金相组织及各种力学性能。结果表明,耐侯钢双相化后的显微组织由多力形等轴素体晶粒和不规则岛状马氏体组成,且原始组织对其有很大影响;两种热轧耐钢双相化热处理前后的显微组织和力学性能均无明显的各向异性。研究发现,双相化加热温度对马氏体含量、屈服现象、屈服强度、抗拉强度、屈强比、延伸率及加工硬化指数（ｎ值）等双相化后钢的组织性能均有显著影响。根据试验结果     

超声波均匀沉淀法制备Y2O3∶Eu3＋纳米晶及其荧光性能

在超声波作用下,使用均匀沉淀法制备了纳米Y2O3∶Eu3＋荧光粉,考察反应物配比、溶液pH值、反应时间、煅烧温度等制备条件对产物晶粒尺寸及产率的影响.利用X射线粉末衍射（XRD）、等离子体原子发射光谱（ICP-AES）、透射电镜（TEM）和荧光光谱等测试手段表征产物,结果表明,该法制得的纳米Y2O3∶Eu3＋荧光粉颗粒为球形,粒度分布均匀,平均粒径约为30 nm.与微米晶相比,该纳米晶的激发光谱发生明显红移,电荷迁移态最大值（CTS）红移12 nm,发射光谱中发射主峰蓝移8 nm.     

公路桥涵台背回填材料研究现状综述

为了减少公路桥涵台背回填病害,对台背回填材料和主要处理措施的研究现状进行了总结和评价。从构造差异、地基沉降、回填材料的压缩变形等方面分析了台背回填病害的主要原因,对常用工程措施及其效果进行了总结,包括桥头搭板、地基处理、反开挖填贫混凝土和压密注浆等,对石灰土、砂砾、风积砂、陶粒粉煤灰混凝土、泡沫混凝土、土工格栅、土工格室加筋体、EPS夹层等常用台背回填材料的性能及其效果进行了比较与评价。研究认为台背回填材料的选取应该就地取材,采用新技术对现有材料进行加筋和改性,建议重点研究EPS夹层与格栅加筋的综合运用技术和新型轻质回填材料的开发与应用技术,有效预防桥头跳车病害的发生,提高公路使用性能。     

高速公路扩建工程材料再利用施工技术及效益分析

为节省高速公路扩建工程中施工材料,可以对原本旧路面破除的材料进行循环利用.唐山至天津高速公路扩建工程破除材料全部利用再生技术,取得了良好的经济、社会效益,值得在同行中推广.     

Study on the Formation of η Phase During TIG Welding

The paper studied the effect of Ni-Fe-C filler materials on the η phase formation during TIG welding of WC-30Co and 45 steel. ηphase's morphology and forming condition were discussed using BEI method. The properties of the weld joints were also measured using microhardness measurement and four-point bending measurement. The results show that the weld joints of WC-30Co/45 steel can be obtained by TIG welding using different Ni-Fe-C materials as filler materials, and ηphase formed in the joints is M6C, M12C type carbides. The poor carbon content of the W-Co-C system resulted from the C diffusion and the high ingredient Fe are the two vital factors inducing to ηphase formation. It can be restricted by the addition of C element into Ni-Fe material. When carbon content is 0.01 % in filler material, bend strength σbb of weld joint is 908 MPa. However, when carbon content increases to 0. 41% in filler material, bend strength σbb is 1 260 MPa.     

A method for determining surface free energy of bamboo fiber materials by applying Fowkes theory and using computer aided machine vision based measurement technique

The purpose of this study is to develop a standard methodology for measuring the surface free energy (SFE), and its component parts of bamboo fiber materials. The current methods was reviewed to determine the surface tension of natural fibers and the disadvantages of techniques used were discussed. Although numerous techniques have been employed to characterize surface tension of natural fibers, it seems that the credibility of results obtained may often be dubious. In this paper, critical surface tension estimates were obtained from computer aided machine vision based measurement. Data were then analyzed by the least squares method to estimate the components of SFE. SFE was estimated by least squares analysis and also by Schultz?? method. By using the Fowkes method the polar and disperse fractions of the surface free energy of bamboo fiber materials can be obtained. Strictly speaking, this method is based on a combination of the knowledge of Fowkes theory. SFE is desirable when adhesion is required, and it avoids some of the limitations of existing studies which has been proposed. The calculation steps described in this research are only intended to explain the methods. The results show that the method that only determines SFE as a single parameter may be unable to differentiate adequately between bamboo fiber materials, but it is feasible and very efficient. In order to obtain the maximum performance from the computer aided machine vision based measurement instruments, this measurement should be recommended and kept available for reference.     

大鼠附睾上皮内ACP及NSE与过剩精子处理的关系初探

目的　研究大鼠附睾上皮细胞PAS阳性物质的性质 ,以及与溶酶体的酸性水解酶、附睾腔内过剩精子消化处理之间的关系 ,借以阐明附睾上皮处理过剩精子的机制。方法　用组织化学的方法显示PAS阳性物质、非特异性酯酶 (NSE)和酸性磷酸酶 (ACP)并研究其相互关系。结果　PAS阳性颗粒分布于PAS阳性细胞的核下区、核上区或充满整个胞质 ,也可见于附睾管腔内 ,尤其是附睾上皮近腔面 ,呈条带状 ;NSE、ACP阳性颗粒均位于胞质的核上方及附睾上皮的近腔面。结论　NSE、ACP与PAS的染色结果一致 ,说明附睾上皮除吞噬精子外 ,还可能分泌溶酶体酶进入附睾上皮的近腔面以初步处理精子 ,而精子残骸穿过附睾上皮进入间质可能进一步被巨噬细胞系统消化处理     

复合纳米二氧化钛的制备及光催化降解罗丹明B

以Ti（OC4H9）4和Si（OC2H5）4为原料,采用溶胶-凝胶法制备纳米TiO2-SiO2复合材料.通过光催化降解罗丹明B实验,确定制备纳米TiO2-SiO2复合材料的最佳条件,即Ti∶Si=1∶0.5,煅烧温度为500℃,制备溶胶pH取5~6.通过SEM测试,发现纳米复合材料的基本粒子为分散均匀的球形颗粒状结构;XRD分析结果表明,复合材料中TiO2主要以锐钛矿晶型存在,颗粒粒径在10~30 nm.光催化降解实验表明,按照最佳条件制备纳米TiO2-SiO2复合材料的光催化降解效果较好,在日光照射90 min后,对罗丹明B的降解率可以达到100%.     

MgO的活性及原料配比对氯氧镁水泥结构的影响

通过采用高温煅烧菱镁矿制备活性氧化镁,利用柠檬酸法测定其活性,采用XRD及SEM技术分析了原料配比对镁水泥微观结构和形貌的影响.结果表明,MgO煅烧温度为800℃时活性最好;镁水泥结构随着MgO含量增加变得更加致密,且原料配比为M5.5/H12时致密性最好;镁水泥结构随着水含量的增加而变得疏松,原料配比为M4.5/H15时结构最差;原料配比为M6.5/H12时,MgO煅烧温度对的镁水泥结构影响不大,原料配比为M4.5/H12时,MgO煅烧温度为850℃时镁水泥致密性最好.     

汶川震区桃关沟2013-07-10泥石流成灾机理

针对2013年7月10日持续强降雨导致汶川震区桃关沟暴发特大型泥石流,通过现场勘查和试验,分析了桃关沟泥石流暴发的物源、降雨和地形条件,研究了泥石流的起动、流通和堆积过程.研究结果表明,地震对沟域内岩土体的震动破坏是震后泥石流频繁暴发的根源,其成灾机理体现出崩滑物源、坡面物源和沟道物源三者的启动及相互叠加,从发展趋势看,桃关沟泥石流正处于高频发育阶段,仍存在暴发大规模泥石流的可能性.      

基于数据挖掘的危险货物运输风险驾驶行为聚类分析

不良驾驶行为(车速过高，车速变化过快等)影响危险货物及车辆的稳定性，是导致危险货物运输事故频发且后果严重的重要原因. 基于对营运车辆联网联控系统海量数据的分析处理，根据其属性提取8 个驾驶行为量化指标，采用因子分析和模糊C均值聚类相结合的方法，实现对危险货物运输车辆驾驶员风险驾驶行为的科学聚类. 结果表明，危险货物运输车辆驾驶行为特征可有效聚为急加减速、超速驾驶和变速驾驶3 种行为，且在每种驾驶行为下实现对驾驶员安全等级的分类. 由此可以识别风险较高的驾驶员，这对危险货物运输企业和行业管理部门有重要参考意义.     

复合材料在轨道交通车辆中的应用与展望

围绕玻璃纤维、碳纤维、铝基陶瓷等复合材料在轨道交通车辆中的应用展开了综述；介绍了针对上述复合材料开展的基础与应用研究历程及进展，分析了应用在大型复合材料构件的结构特点；针对头车/司机室、中间车车体、转向架、制动结构、其他结构，系统性地总结整理了复合材料种类、成型工艺、设计方法、优化方法等，全面阐述了复合材料在轨道交通车辆各个部件上的应用情况，并对目前应用存在的问题和未来应用发展方向进行了探讨。研究结果表明:复合材料的主要研究方法以理论研究为基础，在大型结构件中以有限元仿真研究为主，应用多尺度研究方法深入分析复合材料在微观、细观和宏观层面的性能；将复合材料应用到结构中时，在兼具刚度和轻量化的条件下，多采用三明治结构；复合材料之间、复合材料与金属材料的连接结构多采用胶接连接、螺栓连接、胶-螺混合连接等，其中混合连接结构强度大，稳定性高，在工程中应用最为广泛；复合材料已在轨道交通车辆中有一定的应用，纤维复合材料多用于头车/司机室、车体、转向架，而铝基陶瓷复合材料多用于制动结构；在未来应建立适用于轨道交通行业的复合材料相关标准与规范，研发新工艺，采用整体设计模式，扩大复合材料的使用范围，将更多高性能、低成本和轻质化的复合材料应用到轨道交通车辆中。